This work ties in with the investigation of the intermediate valent states and valence fluctuations in certain europium based intermetallic systems. Valence fluctuations are a property of the electronic system of a compound that is possibly accompanied by structural effects, which, in some cases, are quite noticable. By assuming how the changes in the electronic system and in the crystal lattice are connected, valence _uctuations of europium are believed to be a possible probe for the theory of quantum critical elasticity, which is investigated on by the SFB TRR 288 (Frankfurt, Mainz, Karlsruhe, Bochum, Dresden).
Here, the proceedings in growing single crystals of di_erent compounds related to this _eld of research are reported. This includes the ThCr2Si2 (122) type compounds EuPd2Si2 as well as the doping series EuPd2(Si1-xGex)2, the Europium based ternary Phosphides EuFe2P2, EuCo2P2, EuNi2P2 and EuRu2P2, and attempts to grow compounds of a derived 1144 structure by ordered substitution of half the Europium, EuKRu4P4.
The largest part of this work focusses on the EuPd2Si2 system, which exhibits intermediate valent europium and a temperature dependent transition between two di_erent intermediate valent states of europium. Crystals of this system were grown using the Czochralski method with a levitating melt and an europium excess flux after a two step prereaction process. Also, explorations of a PdSi-rich flux and external flux methods are reported. Ten Czochralski grown experiments, in six generations iteratevely seeded by the previous generation, were prepared.
Thermodynamical and structural analyses of the crystals located the transition between the di_erent intermediate valent states of europium between 140K and 165 K, transitioning from a high temperature Eu2.3+ state to a low temperature Eu2.7+ state, and classified it as a second order transition. To this transition a lattice anomaly of the a-parameter collapsing about 2% is connected, while the c-parameter remains largely unaffected. Large differences between individual samples can be explained by combining thermodynamical and structural analyses with compositional analysis, revealing the valence transition temperature as strongly dependent on the sample composition and Pd-Si site interchanges.
Searching to change the character of the valence transition to first order, silicon was substituted by germanium to introduce negative pressure. Germanium substituted samples of EuPd2(Si1-xGex)2 were grown using the Czochralski method with the optimized parameters from the growth experiments for the undoped compound. Samples were prepared with a nominal substitution of x = 0.05, x = 0.10, x = 0.15, x = 0.20 (twice) and x = 0.30. For the EuPd2(Si1-xGex)2 system, a phase diagram for the europium valence states is derived from chemical and thermodynamical characterizations.
n ternary europium phosphides EuT2P2, the position of the compounds in the generalized phase diagram and the question of long range magnetic order or valence transition appear connected to an isostructural transition of the tetragonal crystal structure, drastically decreasing the length of the c-parameter while establishing covalent bonds between phosphorus atoms of different interlayers of the structure, the so called ‚collapse‘. While EuFe2P2, EuT2P2 and EuCo2P2 display both long range magnetic order and a non-collapsed crystal structure, EuNi2P2 shows both a valence transition between two intermediate valent states at a characteristic temperature of 36K - accompanied by a small lattice anomaly of the a-parameter shrinking about 0.2% - and a collapsed crystal structure. Samples of EuFe2P2, EuCo2P2 and EuNi2P2 were grown in tin flux and using solid-solid sintering approaches.
Single crystals of EuFe2P2, EuCo2P2 and EuRu2P2 were investigated at ESRF in Grenoble with single crystal X-ray di_ractometry on a pressure range up to 15GPa and at temperatures down to 15K to investigate the nature of the structural transitions in the compounds. While in EuCo2P2 the structural transition occurs as a transition of first order at all temperatures (e.g. at 2GPa for 15 K), in EuFe2P2 and EuRu2P2 the structural collapse evolves over a broad pressure range up to 8GPa and as a transition of second order troughout the temperature ranges, albeit seeming to sharpen at lower temperatures. From the crystallographic data, elastic constants of the compounds could be derived, revealing EuFe2P2 and EuRu2P2 as unexpectedly elastic materials.
In order to probe the structural collapse at more accessible pressures, crystals with a sturcture derived from the 122 structure, but with ordered 50% substitution of europium and hence altering the symmetry from I4/mmm to P4/mmm in a 1144 structure, were exploratively pursued. Different experiments to obtain EuAT4P4 (with A = K, Rb, Cs and T = Fe, Ru) from binary or ternary prereactants or directly from the elements remained largely unsuccessful.
Die vorliegende Arbeit befasst sich mit der Untersuchung der Transporteigenschaften inklusive Ladungsträgerdynamik von quasi-zweidimensionalen organischen Ladungstransfersalzen. Diese Materialien besitzen eine Schichtstruktur und weisen eine hohe Anisotropie der elektrischen Leitfähigkeit auf. Aufgrund der geringen Bandbreite und der niedrigen Ladungsträgerkonzentration gehören die Materialien zu den stark-korrelierten Elektronensystemen, wobei sich die elektronischen Eigenschaften leicht durch chemische Modifikationen oder äußere Parameter beeinflussen lassen. Die starken Korrelationen resultieren in Metall-Isolator-Übergängen, die sich beim Mott-isolierenden Zustand in einer homogenen Verteilung und beim ladungsgeordneten Zustand in einer periodischen Anordnung der lokalisierten Ladungsträger manifestieren.
Mithilfe der Fluktuationsspektroskopie, die sich mit der Analyse der zeitabhängigen Widerstandsfluktuationen befasst, konnten im Rahmen dieser Arbeit neue Erkenntnisse über die Ladungsträgerdynamik in den verschiedenen elektronischen Zuständen gewonnen werden. Die Metall-Isolator-Übergänge in den untersuchten Systemen, die auf den Molekülen BEDT-TTF (kurz: ET) bzw. BEDT-TSF (kurz: BETS) basieren, sind von der Stärke der strukturellen Dimerisierung abhängig und wurden durch die Kühlrate, eine Zugbelastung sowie durch die Ausnutzung des Feldeffekts beeinflusst.
In den Systemen κ-(BETS)₂Mn[N(CN)₂]₃, κ-(ET)₂Hg(SCN)₂Cl und κ-(ET)₂Cu[N(CN)₂]Br sind die Donormoleküle als Dimere angeordnet, sodass aufgrund der effektiv halben Bandfüllung bei genügender Korrelationsstärke häufig ein Mott-Übergang auftritt. In κ-(ET)₂Hg(SCN)₂Cl führt eine schwächere Dimerisierung jedoch zu einem Ladungsordnungsübergang, der mit elektronischer Ferroelektrizität einhergeht. Dabei wird die polare Ordnung durch eine Ladungsdisproportionierung innerhalb der Dimere verursacht. Die Widerstandsfluktuationen zeigen am ferroelektrischen Übergang einen starken Anstieg der spektralen Leistungsdichte, eine Abhängigkeit vom angelegten elektrischen Feld sowie Zeitabhängigkeiten, die auf räumliche Korrelationen der fluktuierenden Prozesse hindeuten. Diese Eigenschaften wurden ebenfalls für das System κ-(BETS)₂Mn[N(CN)₂]₃ beobachtet. Hierbei wurden mithilfe der dielektrischen Spektroskopie ebenfalls Hinweise auf Ferroelektrizität gefunden, während durch die Analyse der stromabhängigen Widerstandsfluktuationen die Größe der polaren Regionen abgeschätzt werden konnte. Das System κ-(ET)₂Cu[N(CN)₂]Br, das in einer Feldeffekttransistor-Struktur vorliegt, erlaubt neben der Untersuchung des Bandbreiten-getriebenen Mott-Übergangs durch die Zugbelastung eines Substrats auch die Beeinflussung der elektronischen Eigenschaften durch die Änderung der Bandfüllung mittels elektrostatischer Dotierung. Hierbei wurden starke Abhängigkeiten des Widerstands von der Gatespannung beobachtet und Ähnlichkeiten der Ladungsträgerdynamik zu herkömmlichen Volumenproben gefunden.
Bei den Systemen θ-(ET)₂MM'(SCN)₄ mit MM'=CsCo, RbZn, TlZn tritt ein Ladungsordnungsübergang auf, der eine starke Abhängigkeit von der Kühlrate zeigt. Durch schnelles Abkühlen lässt sich der Phasenübergang erster Ordnung kinetisch vermeiden, wodurch ein Ladungsglaszustand realisiert wird. Dieser metastabile Zustand zeigt neuartige physikalische Eigenschaften mit Ähnlichkeiten zu herkömmlichen Gläsern und wurde als Folge der geometrischen Frustration der Ladung auf einem Dreiecksgitter diskutiert. Im Rahmen dieser Arbeit konnte die Ladungsträgerdynamik in den verschiedenen Ladungszuständen von unterschiedlich frustrierten Systemen verglichen werden. Zur Realisierung sehr schneller Abkühlraten wurde dafür eine Heizpulsmethode verwendet und weiterentwickelt. Der Ladungsglaszustand zeigte dabei für verschiedene Systeme ein deutlich niedrigeres Rauschniveau als der ladungsgeordnete Zustand. In Kombination mit Messungen der thermischen Ausdehnung und kühlratenabhängiger Transportmessungen wurde in den Systemen mit der stärksten Frustration die Existenz eines strukturellen Glasübergangs nachgewiesen, der von einer starken Verlangsamung der Ladungsträgerdynamik begleitet wird. Diese Erkenntnisse werfen ein neues Licht auf die bisherige rein elektronische Interpretation des Ladungsglaszustands und heben den Einfluss der strukturellen Freiheitsgrade hervor.