Refine
Year of publication
Document Type
- Doctoral Thesis (30)
Has Fulltext
- yes (30)
Is part of the Bibliography
- no (30)
Keywords
- Totalreflexionsröntgenfluoreszenzanalyse (4)
- Halbleiteroberfläche (3)
- Kontamination (3)
- Kraftmikroskopie (3)
- Silicium (3)
- Chemische Analyse (2)
- Monoschicht (2)
- Niob (2)
- Nitrid (2)
- Rapid Thermal Processing (2)
Institute
- Biochemie und Chemie (26)
- Pharmazie (2)
- Biochemie, Chemie und Pharmazie (1)
- Biowissenschaften (1)
Development of chromium(VI)-free defect etching solutions for application on silicon substrates
(2008)
Die Erforschung der neuartigen Materialien BST, PZT und SBT für den Einsatz in neuartigen Speichertechnologien wie dem FeRAM besteht aus vielen unterschiedlichen Teilbereichen. Im Rahmen dieser Dissertation wurden primär zwei Hauptbereiche analysiert. Als Erstes wurden sowohl die Mechanismen der Oberflächenausbildung (Wachstumsverfahren, Prozeßparameter, Substrat Einflüsse) von einzelnen Filmen, als auch die Wechselwirkungen der Schichten untereinander und deren Auswirkung auf das Schichtsystem, untersucht. Im zweiten Schritt wurde das elektrische Verhalten, und die auftretenden Phänomene sowohl qualitativ als auch quantitativ erfaßt und bewertet. Als Elektrodenmaterial für die di/ferroelektrische Speicher kann nicht wie gewohnt dotiertes Silizium/Polysilizium verwenden werden. Da Platin den chemischen und thermischen Belastungen bei der Herstellung dieser Filme besonders gut gewachsen ist, wird es bevorzugt als Elektrode eingesetzt. Bei dem Aufbau der Pt-Elektrode erfolgt die größte Veränderung des Systems durch die RTP-Oxidation des reaktiven Titans. Die Rauhigkeit des vorher sehr fein kristallinen Ti-Films steigt auf das Vierfache bei einer gleichzeitigen Verdreifachung der Korngröße. Da in vielen Bauelementen Si oder Poly-Si in Kombination mit einer Ti/TiN-Barriere als Basis für den Pt-Film fungieren, wurde bei den nächsten Experimenten der Einfluß des Substrates und der TiN-Sputtertemperatur auf die Topologie/Morphologie der Elektrode untersucht. Nur durch Anpassung der TiN Sputterleistung, eine niedrige Substrattemperatur und der Kombination aus N2-RTP Temperung (nach TiN) und O2-Temperung (nach Pt), gelingt es die Rauhigkeit und Kristallitgrößen des entstandenen Filmsystems zu minimieren. Bei der Charakterisierung der di/ferroelektrischen Materialien BST, PZT und SBT wurden zum einen das Wachstum und die beim Aufbau der Schichten auftretenden Phänomene anhand verschiedener Abscheidungstechniken untersucht/verglichen. Zum anderen sind mehrere Schichtdicken, Schichtabfolgen und eine Reihe unterschiedlich getemperter Proben analysiert worden. Die mittels Sputtern hergestellten BST Filme belegen, dieses Material hat typischerweise ein columnares Kristallwachstum und läßt sich sehr fein kristallin aufbringen. Bei der reaktiven Abscheidung aus der Gasphase (MOCVD) hat sich schnell gezeigt, das komplexe Material System BST reagiert bereits bei Variation eines Parameters extrem unterschiedlich. So findet bei einer hohen Substrattemperatur (690°C) ein fließender Übergang vom zwei dimensionalen (2D, Frank-van der Merwe), zum drei dimensionalen (3D, Stranski-Krastanov) Wachstum statt. Wird BST bei 600°C abgeschieden, liegt von Anfang an ein gemischter 2D/3D Schichtaufbau vor, der überwiegend in einen 3D inselartigen Aufbau (Vollmer-Weber) übergeht. Senkt man die Temperatur auf 450°C, bildet sich auf der Oberfläche Haze, der durch eine instabile Gasphasenreaktion an der Oberfläche entsteht und sich hauptsächlich aus Strontium- und Bariumoxid zusammensetzt. Gesputtertes PZT besitzt im Vergleich zu BST eine um den Faktor 6 höhere Wachstumsrate, und bildet zweimal so breite Kristallite aus. Es hat eine relativ feinkörnige Struktur und seine Kristalle wachsen wie beim BST columnar auf. Die MOD Technik erzeugt einen relativ homogenen SBT-Schichtaufbau mit Korngrößen bis zu 135 nm. Erst nach dem Ferroanneal entstehen bis zu dreimal größere Kristalle, die von markanten Korngrenzen getrennt werden und große Kristallflächen mit Unterstrukturen haben. Die mit der MOCVD Methode hergestellten SBT-Proben zeigen teilweise Wachstumsphänomene in Form von Hillocks, die im EDX allerdings keine Unterschiede in der Zusammensetzung aufweisen. Die systematische Untersuchung der Wechselwirkung von Temperatur (600-800°C) und Schichtdicke (ca. 80-175 nm) bei konstanter Temperzeit hat ergeben, daß die Filme bei einem 600°C Ferroanneal kleine Hillocks besitzen, die erst ab 700°C nicht mehr zu beobachten sind. Neben der topographischen Analyse von Di- und Ferroelektrika gibt es einen zweiten sehr wichtigen Aufgabenbereich, die elektrische Charakterisierung dieser Materialien. Da alle herkömmlichen Verfahren diese Daten nur Integral erfassen können, eröffnet die Rastersondenmikroskopie hier erstmalig die Chance, sowohl Topographie als auch elektrische Parameter simultan und mit hoher Ortsauflösung (10-50 nm) zu analysieren. Die ersten Versuchsreihen wurden mit dem EFM gemacht und haben sich mit dem Polarisationsverhalten von PZT und SBT beschäftigt. Zu diesem Zweck wurde ein Experiment entwickelt, bei dem das Ferroelektrikum durch gezielte Polarisationen in zwei definierte Zustände entgegengesetzter maximaler Polarisation versetzt wird. Die Ergebnisse konnten mit dem Oberflächenpotential Mikroskop reproduziert werden, allerdings reagiert das Oberflächenpotential Mikroskop deutlich stärker auf freie Ladungen als das EFM. Um zwischen Ladungsartefakt und realer Beobachtung unterscheiden zu können, wurde ein Verfahren zur Konditionierung und Ladungsentfernung der Probe entwickelt, ohne die Probe merklich zu manipulieren. Da bei den EFM-Untersuchungen viele verschiedene elektrostatische Phänomene aufgetreten sind, ist eine generelle Betrachtung zur Fragestellung, was bildet das erhaltene EFM-Signal eigentlich ab, gemacht worden. Dazu wurde ein deutlich vereinfachtes Ladungsmodell vorgestellt, das den Polarisationsvorgang mit seinen unterschiedlichen Einzelprozessen beschreibt. Zusammenfassend ist zu sagen, daß EFM ein elektrostatisches Gesamtfeld detektiert, das aus verschiedenen Komponenten besteht, die in der Regel qualitativ und nicht quantitativ miteinander verknüpft sind. Im Gegensatz zu makroskopischen Messungen haben zeitabhängige Untersuchungen an SBT gezeigt, die abgebildete Polarisation verringert sich bereits nach wenigen Tagen signifikant. Eine Erklärung für den Signalverlust ist die Annahme, daß sich über die Zeit primär nur die SBT-Oberfläche verändert, da ihr die elektrisch und chemisch stabilisierende Pt-Elektrode fehlt. Eine weitere Überlegung geht davon aus, durch die EFM-Spitze hat eine wesentlich höhere Feldstärke auf das Ferroelektrikum eingewirkt und das Material dadurch stärker gestreßt. Die Untersuchung der temperaturabhängigen Relaxation von ferroelektrischen Filmen liefert weitere interessante Erkenntnisse. Ohne obere Pt-Elektrode kann man bereits ab 130°C einen deutlichen Polarisationsverlust beobachten (Curie-Punkt SBT: 310°C). Die Temperversuche sprechen damit für die Hypothese, durch die fehlende obere Elektrode wurde bei der Polarisation erhöhter Streß in das SBT eingeprägt und das System hat darauf mit stark beschleunigter Relaxation reagiert. Es kann jedoch nicht abschließend geklärt werden, was auf das Materialverhalten einen größeren Einfluß ausübt, die Oberflächenladungen oder die fehlende obere Pt-Elektrode. In weiteren Experimenten wurde die Bildung der ferroelektrischen Phase und deren Störungen untersucht. Versuche mit unterschiedlicher Ferroannealtemperatur bei MOD SBT-Schichten haben gezeigt, die Kristallphasenbildung wird hauptsächlich von der Annealtemperatur gesteuert. Bei einer Temperatur von 600°C wird nur eine partielle Phasenumwandlung erzielt, dagegen liegt bei 800°C eine vollständige Umwandlung in den pseudotetragonalen Perowskit vor. Die Untersuchung eines mittels MOCVD-Verfahren abgeschiedenen SBT-Films ergab eine nicht vollständig polarisierte Oberfläche. Da sich bei einer Substrattemperatur von 640°C primär eine a/b-Kristallachsenorientierung ausbildet, die Probe jedoch nur partiell polarisierbar war, ist höchstwahrscheinlich die Substrattemperatur während der Abscheidung zu niedrig gewesen. Zum Abschluß der Versuche wurde der Polarisationsbereich zunächst auf wenige Mikrometer verkleinert und schließlich sogar auf einzelne Kristalle eingeschenkt. Obwohl es gelingt, einzelne Kristalle zu polarisieren, zeigen diese Experimente deutlich die Limitierungen des EFMs auf. Die ersten Messungen mit dem Piezoresponse-SPM haben ergeben, daß es möglich ist, subkristalline Polarisationsstrukturen ohne nennenswerte Topographieartefakte und „Übersprechen“ abzubilden. Mit dem C-AFM ist in sehr hoher Orts- und Stromauflösung das Leckstromverhalten von BST, PZT und SBT untersucht worden. Da diese di- und ferroelektrischen Materialien eine polykristalline Struktur haben, treten neben Fehlertypen wie Fremdatomdefekten und Leerstellen auch noch eine Vielzahl anderer Kristallbaufehler (Versetzungen, Korngrenzen, ...) auf, die zu erhöhten Leckströmen führen. Auch die Morphologie der Filme beeinflußt das elektrische Verhalten der Materialien. Bei den als Erstes vermessenen BST-Proben ist eine starke Schichtdicken- und Feldstärken-Abhängigkeit zu beobachten. So wird das Leckstromverhalten bei dünnen BST-Proben und niedrigem Potential von extrinsischen Fehlern in Form von Fremdatomdefekten, Leerstellen und verschiedenen Kristallbaufehlern dominiert. Erhöht man allerdings die Feldstärke, so bestimmen die intrinsischen Fehler die Leckstrompfade, da durch das hohe Potential die Bandstruktur solange degradiert bis ein elektrischer Durchbruch vorliegt. Bei höheren Schichtdicken (70 nm) werden durch den intrinsischen Streß des Films hervorgerufene Leckströme erkennbar. Sie treten erst ab einem kritischen Zug- oder Druckstreßniveau in Insel/Domänen-ähnlicher Form auf, der in der topographischen Aufnahme nicht sichtbar ist. Im Gegensatz zu amorphen Materialien wie dem SiO2 spielt bei BST, PZT und SBT die Filmdicke nur eine untergeordnete Rolle, da eine partielle Dünnung nicht automatisch einen erhöhten Leckstrom zur Folge hat. Da ferroelektrische Materialien eine Leckstromgenerierung besitzen die komplexer ist, und einem anderen Zeitablauf folgt, als bei einem Dielektrikum, wurde zuerst das ferroelektrische PZT mit dem C-AFM analysiert. Die ersten Untersuchungen an einer PZT-Probe haben allerdings sehr schnell gezeigt, zwischen BST und PZT gibt es keine nennenswerten Unterschiede im Leckstromverhalten. Für die Herstellung von SBT-Schichten werden hauptsächlich das MOD und das MOCVD Verfahren verwendet. Um festzustellen welche der beiden Abscheidetechniken das bessere Leckstromverhalten hat, wurden MOD und MOCVD SBT-Filme charakterisiert. Diese Untersuchungen haben gezeigt, bei MOCVD Filmen treten die Leckströme hauptsächlich in den Bereichen auf, die leicht vereinzelte oder nicht dicht verwachsene Korngrenzen und Kristallecken besitzen. Im Vergleich dazu weisen die MOD Schichten in ähnlichen Bereichen deutlich wenigere und niedrigere Leckströme auf. Den Einfluß von Topologie und Filmdicke hat die Analyse einer mit 90 nm MOD SBT beschichteten Stufe (120 nm) belegt, da dort nur im Kantenbereich extrem erhöhte Leckströme zu beobachten sind. Das Degradationsverhalten von SBT ist außerdem auch noch dickenabhängig. Dies beweisen I/V Spektren, die bei C-AFM Messungen an unterschiedlich dicken MOD SBT-Schichten (90/180 nm) aufgenommen wurden. Es zeigt sich, speziell bei höheren Feldstärken liegt bei der dünnen SBT-Probe (90 nm) eine um den Faktor vier steilere Degradation vor.
Untersuchung möglicher Wege zur Präparation von Nioboxynitriden mittels thermischer Kurzzeitprozesse
(2008)
In dieser Arbeit wurden mögliche Wege zur Präparation von Nioboxynitriden mittels thermischer Kurzzeitprozesse (Rapid Thermal Processing (RTP)) in dünnen Metallfilmen untersucht. Die dafür verwendeten Nb-Filme wurden mittels Magnetronsputtern auf ein thermisch oxidiertes Siliziumsubstrat (SiO2/Si-Substrat) aufgebracht. Die SiO2-Schicht hatte eine Dicke von 100 nm und soll die unerwünschte Reaktion zwischen Si und Nb vermeiden, welche zur Bildung von Niobsiliziden bei der RTP-Temperung führen kann. Um Nioboxynitride zu präparieren wurden Nb-Filme in mehreren Schritten mittels RTP behandelt. Durch die Variation der Ansatzreihenfolge (Oxidation und Nitridierung), der Reaktionsgase (O2, N2, NH3), der Reaktionstemperatur und der Reaktionszeit sowie der Schichtdicke der Proben wurde die Möglichkeit der Bildung von Nioboxynitriden untersucht. Es stellte sich heraus, dass die Bildung von Nioboxynitriden bei der Nitridierung der Nb2O5-Filme in Ammoniak erfolgt. Die Nb2O5-Filme wurden durch die Oxidation der as-deposited Nb-Filme im molekularem Sauerstoff bei 450 °C (nach 5 min Oxidation) bzw. bei 500 °C (nach 1 min Oxidation) hergestellt. Die gebildete Nb2O5-Phase wurde dem orthorhombischen beta-Nb2O5 zugeordnet. Die Oberfläche der Nb2O5-Filme zeigte Rissbildung sowie sichtbare Delamination bzw. Ablösung der Nb-Filme vom Substrat. Dies wird durch das Stressaufkommen im Film bei der direkten Oxidation des as-deposited Films im O2-Strom erklärt. Das Stressaufkommen wird durch eine starke Ausdehnung des Kristallgitters von Niob bei der Bildung des Nb2O5 sowie durch eine hohe Oxidationsrate des as-deposited Nb-Films in O2 hervorgerufen. Das Herabsetzen der Oxidationsgeschwindigkeit verringerte den Stress zwischen dem Metall und Niobpentoxid und verbesserte die Oberflächenqualität des Films nach der Temperung. Eine Herabsetzung der Reaktionsgeschwindigkeit wurde durch die Änderung der Ansatzreihenfolge erreicht. Die Oxidation der vorher nitridierten Nb-Filme führte zu einer langsameren Bildung des Nb2O5 im Vergleich zu den Filmen, die einer direkten Oxidation im O2-Strom ausgesetzt wurden. Dies wurde durch die Barrierefunktion der bei der Nitridierung gebildeten Niobnitride gegen den eindiffundierenden Sauerstoff hervorgerufen. Bei der Oxidation wurde die Diffusion des Sauerstoffes im nitridierten Film durch den Stickstoff gehemmt, was zu einer Abnahme der Oxidationsgeschwindigkeit und somit zu einer langsameren Bildung des Nb2O5 führte. Die Oxidation der zuvor nitridierten Filme führte zu wesentlich niedrigerem Stress zwischen dem Niob und den gebildeten Oxidphasen als zwischen dem Niob und dem Niobpentoxid bei der direkten Oxidation des Niobs in molekularem Sauerstoff. Die weitere Nitridierung der Filme, bei denen bei der Oxidation der bereits nitridierten Filme die Bildung nur einer Nb2O5-Phase erfolgte, führte zur Bildung von zwei Phasen: Nb4N3 und NbxNyOz. Die Zusammensetzung des gebildeten Nioboxynitrides entspricht am wahrscheinlichsten einer Zusammensetzung von NbN0.6O0.2. Sowohl die 200 als auch 500 nm-Filme zeigten nach der dreifachen Temperung eine hohe Porosität. Die hohe Porosität der Probe wurde durch Gasbildung und -diffusion (H2, H2O) im Innern des Films bei der Temperung des Nb2O5-Films in NH3 verursacht. Die EFTEM/EELS-Untersuchungen zeigten, dass sich beim dünnen 200 nm-Film zwei ausgeprägte Zonen (an der Oberfläche – Nb4N3, im Bulk bzw. am Interface – NbxNyOz) gebildet haben. Beim 500 nm-Film zeigte sich, dass die stickstoffhaltigen sowie stickstoff- und sauerstoffhaltigen Zonen, welche entsprechend Nb4N3 und NbxNyOz zugeordnet wurden, im ganzen Film ziemlich gleichmäßig verteilt sind. Ein Hinweis auf die Bildung eines Nioboxynitrides durch die Nitridierung der unvollständig oxidierten Nb-Filme im molekularen Stickstoff wurde nicht gefunden. Bei diesen Temperungen erfolgte die Bildung von unterschiedlichen Oxid- und Nitridphasen. Es wurde festgestellt, dass die Oxidation sowie die Nitridierung der Nb-Filme zu einem texturierten Wachstum der gebildeten Phasen führten. Die SiO2-Schicht auf dem (100)-orientierten Silizium wirkte sich auf das Schichtwachstum des auf das Silizium aufgebrachten Niobs aus und beeinflusste die Kristallstruktur der entstandenen Nb-Schicht und der bei den RTP-Temperungen gebildeten Phasen. Bei dünnen Schichten, wirkt sich dieser Effekt stärker aus, da der Einfluss des Substrates mit wachsender Schichtdicke abnimmt. Die bei der Oxidation gebildeten Nioboxide stellten eine starke Diffusionsbarriere für den bei der Nitridierung eindiffundierenden Stickstoff dar, was zur Aufstauung von Stickstoff in den an der Oberfläche liegenden Filmschichten führte. Die Analyse der erhaltenen SIMS-Daten zeigte, dass bei der Nitridierung der bereits oxidierten Filme die Diffusion des Stickstoffes zwei gleichzeitig ablaufende Prozesse verursacht. Von einer Seite verdrängt der eindiffundierende Stickstoff den Sauerstoff aus dem Film. Andererseits führt die Diffusion des Stickstoffes aufgrund des Schneepflug-Effekts zur Aufstauung des Sauerstoffes in den tiefliegenden Bereichen des Films. Gleichartige Diffusionsprozesse wurden bei der Oxidation der bereits nitridierten Filme beobachtet. Die Nioboxide, welche am Interfacebereich detektiert wurden, bildeten sich durch die Reaktion zwischen Niob und dem aus der SiO2-Schicht ausdiffundierenden Sauerstoff. Die Gegenwart der schon vorhandenen Nioboxide hemmte allerdings die Ausdiffusion des Sauerstoffes aus der SiO2-Schicht des Substrates im Vergleich zu den unoxidierten Filmen.
In the production of integrated circuits (ICs), photolithography plays a key role in wafer structuring. The basic principle of photolithography is the selective processing of areas (etching, implantation, metallisation etc.) while the others are covered and therefore protected by the resist. After each process step the resist, now modified, has to be removed. In the history of semiconductor manufacturing this has been accomplished with a mixture of H2SO4 and H2O2, H2SO4 and O3 or a plasma etch. As the structure sizes decreased they reached a stage where they had to be exposed to light of shorter wavelengths for the photolithography, going from i-line (365 nm) to DUV (248 nm and 193 nm). This change in wavelength now requires new resists and therewith new stripping methods. Beside the changes in the resist the finer structures are also more sensitive to damages caused by the resist strip. Along with this the demand for cost reduction and environment-friendliness poses a big challenge for modern resist stripping. In this study ozone in deionised water (DI/O3) was the basic chemistry investigated as it is cost efficient in production and disposal as well as environment friendly. Furthermore it is a chemistry known to cause no damage to the wafers. DI/O3 has been successfully applied to strip i-line resists. The challenge now is to find ways and means to make DI/O3 strip even highly implanted DUV resists which currently can only be removed by a plasma etch. To achieve this a detailed understanding of the behaviour of ozone in DI water and the influence of factors both chemical and physical on the stripping efficiency at the different stages in the process is necessary. Along with this, methods which enable the elucidation of resist structures and the changes they undergo during the process of photolithography as well as during the ozone strip have to be developed. This will enable us to understand the mechanisms involved and hence, ideally, develop ozone-based stripping solutions customized for each resist and process step. For this purpose the ozone decomposition in DI water with and without additives was studied via UV-Vis spectroscopy. Radicals generated within the ozone decomposition were trapped and quantified, the resists were studied directly on the wafer with IR and Raman spectroscopy and stripped with DI/O3-mixtures and different setups to find optimum conditions for a complete and damage free resist strip. UV-Vis spectroscopy at 260 nm was used to study ozone decomposition and the factors, both chemical and physical, which influence it. These factors are pH, different additives at the same pH, temperature and mixing of the solution. For the radical determination trapping reactions with MeOH and DMSO both forming CH2O which is further converted to DDL as the detectable species were compared with a variation of the classical iodometric titration acting as an absolute method without the need of calibration. IR spectroscopy proved to be a suitable method for the structural characterisation of the resists and the tracking of the changes undergone during the various processing steps as well as the ozone based stripping. For the stripping with DI/O3 IR spectroscopy delivered well-defined spectra. These displayed significant peak changes which support the assumption of classical ozonolysis as the decomposition mechanism for the unimplanted resist. For the study of the resist crust originating from ion implantation IR was fundamentally unsuitable and was replaced by Raman spectroscopy and microscopy. Raman spectra showed the crust to be of a highly carbon containing structure. Regrettably, the peak assignable to the crust was too broad for the exact composition of the crust to be determined. The wavelength region of the peak corresponds to that of peaks of glassy carbon and highly ordered and conventional graphite. Such a broad peak suggests that the structure of the crust is not uniform but contains more than one carbon modification. As the purpose of all these studies is to enable or improve DI/O3 based resist stripping on unimplanted as well as high-dose implanted resists the removal efficiency of DI/O3 spiked with different additives that alter the pH was studied. For these unimplanted resists the maximum efficiency could be achieved at pH = 5 – 7. Lowering or increasing the pH beyond this range gave poor results. The stripping of highly implanted resists could be achieved only at harsh conditions with a high pH-level of 12 - 13 with a narrow process window showing no stripping at lower pHs and severe damages at higher levels. The principle application of DI/O3 stripping chemistry could be proved but the currently required process time unfortunatelly is too long for commercial application and needs further optimisation.
Übergangsmetallboride und -nitride weisen besondere physikalische und mechanische Eigenschaften auf; sie vereinen dabei sowohl die Merkmale von Metallen als auch von Keramiken. Sie besitzen z. B. große Härten, hohe Schmelzpunkte und hohe Abriebfestigkeiten. Des Weiteren sind sie sehr beständig gegenüber Hitze und Korrosion. Sie zeigen eine hohe elektrische und thermische Leitfähigkeit. In den industriellen Anwendungen kommen oft Übergangsmetallboride und -nitride der 4. und 5. Gruppe zum Einsatz. Die Boride und Nitride des Niobs gelten als potentielle Kandidaten für Baumaterialien, welche hohen Temperaturen standhalten sollen. Niobnitride werden zum Teil schon als Beschichtungen von Turbinenmotoren und in der Raumfahrt eingesetzt. Für den industriellen Einsatz als Beschichtung oder Überzug werden in der Regel dünne Filme benötigt, diese werden oft durch Gasphasenabscheidung aufgebracht. Eine alternative Möglichkeit zur Präparation dünner Filme bietet das Rapid Thermal Processing (RTP). Dabei handelt es sich um einen optischen Schnellheizofen, mit dem Aufheiz- und Abkühlraten bis zu 300 K s-1 erreicht werden können. Im Vergleich zu gängigen Ofenprozessen werden Reaktionszeiten deutlich verkürzt. Durch eine Variation der Reaktionsbedingungen ist es möglich, verschiedene Phasen zu erzeugen und deren Abfolge zu beeinflussen. Zusätzlich können metastabile Phasen und Zwischenstufen abgefangen werden. Als Ausgangsschichten für die in dieser Arbeit untersuchte Darstellung von Niobboriden und -nitriden dienten verschiedene B/Nb- sowie B/Nb2N-Schichtsysteme. Diese wurden mittels Magnetronsputtern bzw. Elektronenstrahlverdampfung auf Si/SiO2-Substraten abgeschieden. Die Ausgangsschichten wurden anschließend in der RTP im Temperaturbereich von 600 °C bis 1200 °C getempert. Die Temperungen wurden in Argon bzw. Ammoniak durchgeführt. Zur Charakterisierung der Proben dienten verschiedene Analyseverfahren (XRD, LM, REM, AFM, SIMS, EPMA). Die folgenden Niobboride sowie -nitride können durch Temperungen in der RTP dargestellt werden. Die hexagonale NbB2-Phase entsteht bei Argon- sowie Ammoniaktemperungen in B/Nb-Schichtsystemen mit einem 1 : 1-Schichtdickenverhältnis. Das NbB2 erweist sich unter den untersuchten Reaktionsbedingungen als effektive Diffusionsbarriere gegenüber Sauerstoff, Kohlenstoff, Wasserstoff und Stickstoff. Weitere boridische Phasen werden nur bei Argontemperungen gefunden. Das tetragonale Nb3B2 entsteht in Schichtsystemen mit einem B : Nb-Verhältnis von 1 : 4 und 1 : 10 sowie mit einem Nb : B : Nb-Verhältnis von 5 : 1 : 5. Die Nb3B2-Phase wird durch Kohlenstoff und Sauerstoff verunreinigt. Die Verunreinigungen stammen sowohl aus den Ausgangsschichten als auch aus anderen Quellen (z. B. Trägermaterial). Durch eine Änderung der Sputter- Methode konnten die in den Ausgangschichten vorhandenen Verunreinigungen reduziert werden. In entsprechend neupräparierten Schichtsystemen mit einem B : Nb-Verhältnis von 1 : 4 und 1 : 10 führt dies bei den Argontemperungen zur Ausbildung des orthorhombischen NbB neben dem Nb3B2. Die Bildung der Nitride erfolgt bei den Ammoniaktemperungen der verwendeten Schichtsysteme (außer bei B : Nb im Verhältnis 1 : 1). Welche Phase dabei entsteht ist abhängig von der gewählten Temperatur. Es zeigt sich dabei von niedrigeren zu höheren Temperaturen folgende Phasenabfolge: hexagonales Nb2N -> hexagonales delta‘-NbN -> kubisches NbN. Beim Übergang zwischen den einzelnen Phasen liegen diese nebeneinander vor. Durch die schnellen Aufheiz- und Abkühlraten des RTP-Systems, bildet sich neben dem Nb2N das kinetisch bevorzugte delta‘-NbN. Die Bildung der delta‘-NbN-Phase wird durch die Ähnlichkeit der beiden Elementarzellen unterstützt. Die Nb2N-Phase der B/Nb2N-Bilayer behindert stark die Eindiffusion des Bors, des Stickstoffes und der Verunreinigungen. Damit ist das Nb2N eine relativ gute Diffusionsbarriere. Ein Teil der Nb2N-Schicht weicht dem Druck der Eindiffusion durch Aufstauungseffekte an der Grenzfläche aus. Die aus der Literatur bekannten Phasen Nb3B4 (orthorhombisch), epsilon-NbN (hexagonal) und Nb5N6 (hexagonal) werden bei den untersuchten Reaktionsbedingungen nicht gefunden. Die vorhandenen Verunreinigungen führen vor allem während der Argontemperungen zu verschiedenen Oberflächenphänomenen und zur Ausbildung carbidischer und oxidischer Phasen. Im Zuge der Ammoniaktemperungen spielen die Verunreinigungen eine deutlich geringere Rolle. Die vorgestellten Ergebnisse zeigen, dass durch Temperungen in der RTP verschiedene Niobboride sowie -nitride innerhalb weniger Minuten dargestellt werden können. Jedoch sollten für weiterführende Arbeiten reinere Ausgangschichten bzw. anderer Trägermaterialien verwendet werden um die Ergebnisse weiter zu verbessern.
Es wurden mit phys. Verfahren hergestellte 200 und 500 nm dicke Niobfilme auf oxidiertem Si thermischen Kurzzeitprozessen (RTP) unterzogen, um Oxynitride zu synthetisieren. Die Filme wurden mit verschiedenen Methoden untersucht, um einen Überblick über die entstandenen Produkte und ihre Position im Film zu erlangen. Die Reaktionen wurden in N2 oder NH3 zur Nitridierung mit anschließender Oxidation in O2 durchgeführt. Um eine mögliche direkte Einstufensynthese von Oxynitriden des Niobs zu finden, wurde N2O eingesetzt. Der einfachste Ansatz zur Präparation von Oxynitriden bestand in der Verwendung des N2 und NH3, mit denen die Metallfilme zwischen 600 und 1200 °C umgesetzt wurden. Die Nitridierung mit N2 verlief von der Bildung einer festen Stickstofflösung in Niob bei tiefen Temperaturen über Nb2N zwischen 700 und 1000 °C bis zum Nb4N3 oberhalb 1000 °C. Aus dem Substrat diffundierte Sauerstoff aus, der am Interface Nb/SiO2 zur Bildung einer Oxidzone führte. Der O-Gehalt der Oxide stieg mit steigender Reaktionstemp. Unterhalb 1000 °C wurde NbO gefunden, oberhalb 1000 °C bildete sich NbO2. Eine TEM-Untersuchung gekoppelt mit EEL-Spektrometrie ergab Hinweise auf die Bildung einzelner stickstoffreicher NbOxNy-Kristallite im Bulk der mit N2 umgesetzten Filme. Auch die Nitridierung mit NH3 ergab eine Abhängigkeit des N-Gehaltes der Produkte von der Rkt.-Temperatur. Es erfolgte die Bildung der festen Lösung und Nb2N bei tiefen und mittleren Temperaturen. Ab 900 °C bildete sich NbN, oberhalb 1100 °C wurde vermutlich Nb4N5 detektiert. Im Gegensatz zur Umsetzung mit N2 ergaben genauere Untersuchungen der in NH3 nitridierten Filme keine Hinweise auf die Bildung von Oxynitriden. Die Erstellung von Tiefenprofilen zeigte, dass sich Nitridphasen mit höchstem N-Gehalt an der Oberfläche befanden und der Anteil des Stickstoffs in den Produkten mit zunehmender Tiefe abnahm. Mit Oxiden verhielt es sich umgekehrt: Sobald höhere Oxide gebildet wurden, befanden sie sich am Interface, wo die Sauerstoffkonzentration am höchsten ist. Oxide mit niedrigerem O-Gehalt wurden in der Filmmitte gefunden, wo der Sauerstoff durch die gebildeten Nitride an der Diffusion in Richtung Filmoberfläche gehindert wurde. Die 200-nm-Filme waren formal reaktiver als die 500-nm-Filme. Sie bildeten bereits bei tieferen Temperaturen Phasen mit höherem N- oder O-Gehalt, wofür das geringere zur Verfügung stehende Volumen ursächlich ist. Die Reinheit der Filme führte zu Unterschieden in der Reaktivität: Gesputterte Filme waren reiner als aufgedampfte Filme, die auf Grund der Einlagerung einer geringen Sauerstoffmenge während der Präparation passiviert waren. Dadurch wurde die Diffusion des Stickstoffs eingeschränkt zur Bildung abweichender Phasen zwischen aufgedampften und gesputterten Filmen. Eine Variante der Nitridierung in N2 bzw. NH3 bestand in der Verwendung von O2 als Kühlgas. Die Zugabe des O2 wurde bei unterschiedlichen Temperaturen untersucht. Statt der Einlagerung von Sauerstoff in das Oberflächennitrid unter Oxynitridbildung kam es zur Bildung einer oxidischen Deckschicht. Die Bildung der Schicht erforderte eine Zugabetemperatur höher als 700 °C, bei tieferen Temperaturen war der Film durch das bereits gebildete Nitrid soweit passiviert, dass keine chemische Veränderung stattfand. Die im Nitridierungsschritt gebildeten Produkte wurden als Auswirkung des sog. Schneepflugeffektes unter Kompression in tiefere Filmregionen verschoben. Dies führte zur Bildung von Produkten höherer Stöchiometrie (Nb2N zu NbN oder NbO zu NbO2). Der Einsatz von Lachgas, der zur Einlagerung von N2O-Einheiten in den Metallfilm führen sollte, verlief ergebnislos. Bei Prozesstemperaturen unterhalb 450 °C wurde lediglich die Bildung einer festen Lösung von Sauerstoff im Niob nachgewiesen. Oberhalb 450 °C zersetzte sich N2O unter O-Bildung wodurch der Film oxidiert wurde. Die Umsetzung nitridierter Filme mit N2O und auch dessen Verwendung als Kühlgas brachte keine Veränderung. Die Oberflächennitride waren stabil gegenüber dem N2O. Die Nitridierung der Filme im N2-Strom wurde durch die stoßweise Zugabe von O2 bzw. N2O nach definierten Zeiten variiert. Die Filme bilden nach kurzen Nitridierungszeiten von maximal 20 s gefolgt von einem 10-sek. Sauerstoffstoß eine komplizierte Filmstruktur aus, wie das elementare Tiefenprofil zeigt, das in denselben Filmzonen sowohl Stickstoff als auch Sauerstoff nachweist. Da die Röntgendaten lediglich die Bildung von NbO2 nachweisen, jedoch mit einer leichten Verschiebung der Reflexe zu kleineren Winkeln aufgrund der Einlagerung der größeren Nitridionen in das Oxidgitter, muss es sich bei dem präparierten Film um ein Oxynitrid der Form NbO(2-x)Nx handeln, in dem das Verhältnis von N zu O auf der sauerstoffreichen Seite liegt.
Der Schwerpunkt der vorliegenden Arbeit lag in der Synthese und strukturellen Charakterisierung von sandwichartig aufgebauten kupferhaltigen Organosiloxanen. Diese sollten nach Möglichkeit kristalline Eigenschaften aufweisen und ein interessantes magnetisches Verhalten zeigen. Es galt, die Beziehungen zwischen molekularer Struktur und magnetischen Eigenschaften herauszuarbeiten, um auf der Basis experimenteller Daten dem maßgeschneiderten Design neuer molekularer Magnete näher zu kommen. .... Die in der hier vorgelegten Arbeit erzielten Ergebnisse belegen, dass der Weg zur gezielten Erzeugung molekularer Magnete erfolgreich beschritten wurde. Es wird weiteren Arbeiten vorbehalten bleiben, Cluster der nun vorliegenden Art chemisch so zu verknüpfen, dass daraus polymere Ketten oder Netzwerke entstehen. Deren magnetisches Verhalten lässt erwarten, dass damit möglicherweise neue Materialien zugänglich werden, die dem Anspruch eines molekularen Magneten voll gerecht werden.
Im Rahmen der vorliegenden Arbeit wurden auf dem Gebiet reaktiver Silicium-Spezies folgende apparative und experimentelle Forschungsergebnisse erzielt: Zunächst wurde eine Hochtemperatur-Pyrolyse Anlage entworfen, die mit Hilfe von Hochvakuum-Bedingungen (p< 5x10 hoch -9 mbar) Verdünnungseffekte simuliert, um die in der Gasphase erzeugten Moleküle unter solchen Bedingungen zu studieren, bei denen sie keine Folgereaktionen mit weiteren Partnern eingehen können. In die Apparatur integriert wurde ein Ofen (Tmax ungefähr gleich 1200°C) für die Pyrolyse von Stoffgemischen sowie zur Analyse des erzeugten Molekularstrahls ein Quadrupol-Massenspektrometer (0-300 amu, EI-Quelle, SEV). Es wurden Precursoren synthetisiert, die durch Thermolyse infolge intramolekularer Umlagerungen und Abspaltungen definierter Abgangsgruppen Si=X-Doppelbindungen (X= O, S) ausbilden. Diese Precursoren und ihre Pyrolyseprodukte wurden sowohl in der neuen Anlage als auch mittels eines vorhandenen PE-Spektrometers charakterisiert. Parallel zu den Synthesen wurden quantenmechanische Berechnungen an den Produkten der Pyrolysereaktionen durchgeführt, um ihre Eigenschaften, wie z.B. die Orbitalenergien und ihre Strukturparameter, zu bestimmen. Die Ergebnisse sollten die Interpretation der spektroskopischen Untersuchungen (PE und MS) unterstützen. Im zweiten Teil der Arbeit wurden Fragestellungen bearbeitet, die in anderen Teilprojekten der Arbeitsgruppe von essentiellem Interesse sind. Dabei wurden Lösungen zu Fragestellungen der direkten Si-C-Knüpfung und von Silylen-Reaktionen erarbeitet. Eine Versuchsreihe, die durchgeführt wurde, beschäftigte sich mit den Hochtemperaturreaktionen von SiCl4 und SiF4. Die flüchtigen Ausgangssubstanzen wurden im Pyrolyseofen bei ansteigenden Temperaturen mit pulverförmigem elementarem Silicium oder SiO umgesetzt. Hierbei wurden die Bildungsbedingungen von Dihalogensilylenen in der Gasphase optimiert. In einer weiteren Fragestellung wurden die Thermolyseeigenschaften von Si und SiO untersucht. Beide Feststoffe können ab einer Temperatur von ca. 1000°C und einem Druck von 2x10 hoch -6 mbar atomar bzw. molekular in die Gasphase überführt werden. Dort reagieren sie mit Halogensilanen unter Bildung von Silylenen und Chlorsilanen. Weiterhin wurde eine Disproportionierung von SiO zu Silicium und SiO2 unter hohen Temperaturen beobachtet; konsequenterweise wird dabei Sauerstoff freigesetzt. Weiterhin wurde versucht, die Produkte der Halogensilan-Pyrolyse mit Oxidationsmitteln wie Ethylenoxid zur Reaktion zu bringen. Zuletzt wurden Hydrolyse-Versuche mit SiCl4/SiF4 bzw. :SiCl2/:SiF2 und Wasser untersucht.
Silicon wafers such as Silicon on Insulator (SOI) and strained silicon on Insulator (sSOI) are the essential and basic materials of advanced microelectronic devices. However, they often show various kinds of crystal defects which impair the function of these devices. The most efficient method to date, for detecting such defects and for determining their density, is to delineate them by etching the wafers with a suitable etching solution and characterise them via light optical microscopy. Etch pits are formed at defect sites which are etched at a faster rate than at the perfect lattice. The standard etching solution used for SOI and sSOI is a dilute version of Secco. As Secco contains carcinogenic and environmentally hazardous chromium (VI), the use of which is or will be restricted by law in many countries, suitable chromium (VI)-free etching solutions like Organic Peracid Etches (OPE), modified Chemical Polishing Etches (CP) like CP4 mod and mixtures with organic oxidizing agents like chloranil (CA) have been developed for the successful delineation of various types of crystal defects.
However there are still nanometer-sized defects which are hard to detect or escape detection by this method. Copper decoration is a well known method to magnify these defects. It consists in applying a copper nitrate solution to the back of the SOI or sSOI wafer. On annealing, copper diffuses through the substrate and the BOX (buried oxide) to the SOI/sSOI film and on quenching to room temperature, copper precipitates as copper silicide, SiCu3, foremost at crystal defects where the lattice strain is greater than at perfect lattice sites. These silicides increase the volume in these parts of the crystal lattice and defect magnification occurs. A considerable disadvantage of this method is its tendency for artefact formation, when the copper concentration used is too high, with the copper precipitating at the film surface. The consequence is a higher density of etch pits whereby true defect etch pits cannot be differentiated from those caused by artefacts.
The aim of this thesis is to show that the processes of decorating and etching can be combined successfully to delineate all crystal defects in SOI and sSOI. An ideal result would have been to find a copper decoration procedure that decorates all existing crystal defects at a copper concentration that avoids artefact formation.
Poly(pyrazol-1-yl)borate, die sogenannten Skorpionate, repräsentieren eine der etabliertesten Ligandenklassen in der Koordinationschemie und finden aufgrund ihrer Vielseitigkeit zahlreiche Anwendungen. In den letzten Jahren hat sich ein besonderes Interesse an Bis- und Tris(pyrazol-1-yl)boratliganden entwickelt, die mehrere Skorpionateinheiten im selben Molekül vereinen und dadurch kooperative Effekte zwischen den Metallionen fördern. Diese Liganden können sowohl Einsatz in der homogenen Katalyse als auch in den Materialwissenschaften finden. Die bisher in unserer Arbeitsgruppe entwickelten ditopen Bis(pyrazol-1-yl)borate des Typs L (Abb. 3.1) weisen allerdings eine recht hohe Hydrolyseempfindlichkeit auf, deren Ursache wahrscheinlich im elektronenschiebenden Charakter und der Raumerfüllung der Alkylsubstituenten begründet liegt. Im Rahmen der vorliegenden Arbeit wurden daher zunächst die ditopen Skorpionatliganden M2[3] und M2[6] mit Phenyl- und Pentafluorphenylsubstituenten dargestellt, die in darauf folgenden Hydrolysestudien eine im Vergleich zu L erheblich höhere Beständigkeit gegenüber Feuchtigkeit zeigten. Die Umsetzungen der Liganden Li2[Lpara] (Dissertation Dr. Susanne Bieller; Frankfurt 2005) und Li2[6] mit MnII-chlorid verdeutlichten, dass sich das C6F5-substituierte Heteroskorpionat auch in Bezug auf sein koordinationschemisches Verhalten vom tertButyl-substituierten Liganden unterscheidet. Während Li2[Lpara] mit MnCl2 zu einem chlorid-überbrückten, makrozyklischen, dinuklearen Mangankomplex reagiert, wird mit Li2[6] das in Abb. 3.2 dargestellte Koordinationspolymer {(MnCl2)2(Li(THF)3)2[6]}∞ erhalten. Die Ladung der anionischen Polymerkette wird durch Lithium-Gegenionen ausgeglichen. Um die Bildung von diskreten Komplexen einerseits bzw. von Koordinationspolymeren andererseits gezielt steuern zu können, wurden die mit sterisch anspruchsvollen Pyrazolylsubstituenten versehenen Liganden M2[4], M2[5] und M2[7] (Abb. 3.1) dargestellt. Im Zuge der Kristallisation von Li2[4] zeigte sich, dass diese Verbindung eine hohe Affinität für Chloridionen besitzt. Auch in Anwesenheit eines Überschusses Kronenether führen Spuren des Halogenids zur Ausbildung des in Abb 3.3 gezeigten dinuklearen, chloridverbrückten Lithiumkomplexes Li2Cl[4]. Die ausgeprägte Komplexbildungstendenz lässt Li2Cl[4] im Hinblick auf die Entwicklung von Anionenrezeptoren interessant erscheinen. Komplexe, in denen zwei Metallionen durch zwei Heteroskorpionatliganden in eine makrozyklische Struktur eingebunden werden (Tmeta/para in Abb. 3.4), konnten im Rahmen dieser Arbeit nicht isoliert werden. Ein Hinweis, warum dieses Strukturmotiv ungünstig sein könnte, wurde durch die Charakterisierung des auf einem partiell hydrolysierten Derivat von Li2[Lpara] beruhenden CoII-Makrozyklus Co2[23]2 erhalten. Die Analyse der Strukturparameter dieser Verbindung deutet an, dass die Bildung eines Makrozyklus im Fallder unhydrolysierten Heteroskorpionate aufgrund sterischer Wechselwirkungen zwischen den Pyrazolylringen und der Phenylenbrücke benachteiligt sein sollte. Obwohl zwischen Aryl- und Alkyl-basierte n Heteroskorpionaten erhebliche Unterschiede hinsichtlich ihrer Neigung zur hydrolytischen Zersetzung erkennbar sind, zeigen beide Ligandentypen ähnliche Labilitäten gegenüber der stark Lewis-aziden Verbindung Brommanganpentacarbonyl. Die Reaktionen von Li2[Lpara], Li2[3] und Li2[6] mit Mn(CO)5Br führten zur Spaltung von B-N-Bindungen, die in allen drei Fällen durch Kristallisation des in Abb. 3.5 gezeigten, pyrazolid-verbrückten MnI-Carbonylkomplexes 21 dokumentiert werden konnte. Im Gegensatz zu den Heteroskorpionatliganden zeigen oligotope phenylenverknüpfte Homoskorpionate keine Tendenz, sich unter dem Einfluss von Mn(CO)5Br zu zersetzen. Reaktionen der di- und tritopen Tris(pyrazol-1-yl)borate Li2[15], Li2[16] und Li3[18] lieferten die in Abb. 3.6 dargestellten Mangantricarbonylkomplexe (Mn(CO)3)2[15], (Mn(CO)3)2[16] und (Mn(CO)3)3[18] in guten Ausbeuten. Neben der Darstellung dieser, für materialwissenschaftliche Fragestellungen (Koordinationspolymere, Metallorganische Netzwerke) interessanten Liganden, wurde im Rahmen der vorliegenden Arbeit auch der Frage nachgegangen, ob die Verknüpfung zweier Heteroskorpionateinheiten Auswirkungen auf die katalytische Aktivität entsprechender Rhodium-Cyclooctadien-Komplexe in der Polymerisation von Phenylacetylen hat. Sterisch anspruchsvolle Pyrazolylsubstituenten tragende monotope Rhodium-Cyclooctadien- Skorpionatkomplexe konnten in dieser Reaktion bereits erfolgreich als Katalysatoren eingesetzt werden und lieferten regioselektiv cis-transoid-verknüpftes Poly(phenylacetylen). Zunächst wurden die in Abb. 3.7 dargestellten Rhodiumkomplexe (Rh(cod))2[3] und (Rh(cod))2[6] von Bis(pyrazol-1-yl)boraten, die keine sterisch anspruchsvollen Pyrazolylsubstituenten tragen, synthetisiert. Ähnlich wie der analoge einkernige Komplex Rh(cod)[H2Bpz2 ] zeigten (Rh(cod))2[3] und (Rh(cod))2[6] keinerlei katalytische Aktivität. Daher sollten im Anschluss die mit Phenylpyrazolylgruppen ausgestatteten Derivate (Rh(cod))2[5] und (Rh(cod))2[7] synthetisiert und im katalytischen Prozess eingesetzt werden. Im Verlauf dieser Experimente stellte sich heraus, dass die Reaktionen der Alkalimetallskorpionate Li2[5] und K2[7] mit (Rh(Cl)(cod))2 nicht zu den Zielverbindungen, sondern zur Zersetzung der Ligandgerüste führen. In beiden Fällen konnte das Abbauprodukt 22 isoliert werden (Abb. 3.8). Weitere Untersuchungen ergaben, dass 22 in der Lage ist, Phenylacetylen in guten Ausbeuten und regioselektiv (cis-transoid-verknüpftes Poly(phenylacetylen)) zu polymerisieren. 22 stellt somit ein gut zugängliches und leicht zu modifizierendes Katalysatorsystem dar, dessen Optimierung Thema zukünftiger Untersuchungen sein wird.
Determination of the distribution of halocarbons in the tropical upper troposphere and stratosphere
(2008)
The aim of this thesis was to investigate distributions of 32 volatile chlorinated and/or brominated halocarbons that are currently believed to be present in the tropical upper troposphere and stratosphere and to contribute to stratospheric ozone depletion and also to global warming. For this purpose an analytical system was established, which is capable to measure ultra-low concentrated atmospheric trace gases. A quadrupole Mass Spectrometric (MS) Detector was attached to an existing Gas Chromatograph with pre-concentration system and Electron Capture Detector (ECD). The characterisation of the chromatographic system was significantly enhanced by the subsequent identification of 48 additional volatile organic compounds. Furthermore a Gaussian fit algorithm, which was developed in the workgroup, was applied to the chromatographic signals. This algorithm was proven to reflect peaks quantitatively and to enhance the performance of the integration process – especially the reproducibilities for peaks with a low signal to noise ratio. As it is known that the Electron Capture Detector responds nonlinear the new MS detector was checked for such behaviour and found to respond linear. In logical consistency the complete quantification process including e.g. pre-concentration of trace gases and signal integration can be considered as linear responding within the investigated parameter ranges. Moreover, the long term stability of the targeted halocarbons was proven inside the calibration standard containers over a period of 25 months. Many substances were also found to be stable inside the containers used for storage of air samples but a number of substances showed significant concentration changes. These were mainly CH3Cl (methyl chloride), CH3Br (methyl bromide), CH2Cl2 (dichloromethane), CHCl3 (chloroform), CCl4 (tetrachloromethane), C2Cl4 (tetrachloroethene), CH3CCl3 (methyl chloroform), CH2ClCH2Cl (1,2-dichloroethane) und C2H5Cl (chloroethane). But the number of affected substances and also the corresponding concentration changes varied between the individual containers. A systematic investigation of the influence of possible causes (e.g. air sampling methods, container materials) is recommended. Results from both internal detectors were compared and revealed biases and disadvantages of the ECD caused by its lower selectivity and its nonlinear response behaviour. Consequently the MS detector was chosen for the quantification of atmospheric trace gases. The quantification process was performed relative to externally calibrated air standards. To assess the uncertainties connected with different absolute calibration scales cross-comparisons between calibration standards of three different laboratories were carried out. Most substances’ calibrations agreed within the measurement uncertainties but significant differences were observed for CF2ClBr (H1211), CH3Cl (methyl chloride), CH2Cl2 (dichloromethane), CHCl3 (chloroform), CCl4 (tetrachloromethane) and CH3CCl3 (methyl chloroform). As five of these substances were also observed to show concentration changes inside sample containers it is likely, that such changes are responsible for calibration differences. In addition to the detailed assessment of uncertainties connected with the analytical quantification process a set of air samples was available for measurements. These samples mainly originated from the upper troposphere and lower and middle stratosphere in the tropics and the determined halocarbon quantities were used to investigate their distributions in the respective atmospheric regions. In detail, the altitudinal distributions and interrelations of 17 long-lived halocarbons in the tropical stratosphere were determined and compared with those of other stratospheric regions. Tracer-tracer-correlations of these substances in the tropical stratosphere were found to differ from those in mid- and high-latitudes. Characteristic fit functions relative to CF2Cl2 (F12) which are valid for the tropical stratosphere in 2005 were derived as well as time-independent fit functions of fractional release factors (FRFs) relative to the mean age of air. Both sets of correlations could be used for the parameterisation and evaluation of models and also to reassess the Global Warming Potentials (GWPs) of the corresponding halocarbons which might affect future climate predictions. However, the data set on halocarbons in the tropical stratosphere is still insufficient to investigate the variability of tracer-tracer-correlations and FRFs caused by dynamical and photochemical processes. Therefore it is important for future research to perform additional measurements there and – if possible – to extend the measurements to the upper tropical stratosphere in order to characterise the sink of those halocarbons that are still present in these altitudes. In addition, the amount of chlorine and bromine present in the form of organic compounds inside and above the main stratospheric entrance region (the Tropical Tropopause Layer, TTL) was quantified in the frame of a case study. This was possible because of a cooperation with scientists from the University of East Anglia which carried out measurements of six additional halocarbons leading to a total of 28 quantified target substances. Ten of these substances have short atmospheric lifetimes compared with the mean transport times of tropospheric air to the stratosphere (i.e. lifetimes below 0.5 years) and show non-uniform distributions in the upper troposphere. The contribution of these substances to stratospheric ozone depletion is subject of an ongoing scientific debate. In the performed case study a fraction range of short-lived halocarbons of 6 – 8 % (0.98 – 1.25 ppt) relative to the sum of bromine from organic substances and of 1.1 – 1.4 % (36.6 – 47.1 ppt) for the corresponding sum of chlorine was calculated to enter the stratosphere above Brazil in June 2005. Moreover by combining the data with tropospheric reference data and age of air observations the abundances of inorganic chlorine and bromine (Cly and Bry) were derived. At an altitude of 34 km an amount of 3062 ppt of Cly and 17.5 ppt of Bry from organic source gases was calculated. The latter is significantly lower than Bry mixing ratios inferred from quasisimultaneous BrO measurements at 33 km altitude above Brazil (Dorf, 2005, Dorf et al., 2008). But at the University of East Anglia indications for the presence of unknown brominated organic substances in the TTL were found which might cause this difference. Finally, a major result of this thesis adds to the knowledge of the composition of the troposphere as three Chlorofluorocarbons (CFCs) were first observed. Trifluorochloroethene, 3-chloropentafluoropropene and 4,4-dichlorohexafluoro-1-butene were found in air samples collected at the Taunus Observatory near Frankfurt (Main) and the Jungfraujoch High Altitude Research Station in Switzerland (Laube and Engel, 2008). Identification was possible because of an air plume containing high concentrations of these substances. It is suggested that the abundances found on this occasion originated from a local source. The atmospheric lifetimes of these substances are expected to be rather short as they contain a double bond. A quantitative calibration could only be derived for trifluorochloroethene but not for the other species by now. Thus, a relative sensitivity method was derived to get a first indication of the observed atmospheric abundances. All three CFCs could also be detected in air masses representative of background conditions, though with much lower concentrations. These species and some of their degradation products are toxic and could also be relevant for stratospheric and tropospheric ozone depletion. It is important to find out more about their atmospheric distributions, lifetimes, sinks and sources and their ability to reach the stratosphere to assess their possible influence on the global atmosphere. This will be done in the frame of the project "CLEARFOGG – Checking Layers of the Earths AtmospheRe For halogenated Ozone-depleting and Greenhouse Gases". This research project aims to perform a systematic scan of the atmosphere because there are indications for the presence of a number of halogenated organic compounds which are unknown by now. It was recently decided to be funded by the British National Environmental Research Council and will be carried out at the University of East Anglia mainly by the author of this thesis.
Arzneistoffe sind mit einer Vielzahl an anorganischen Elementen im Spurenbereich kontaminiert. Die Elementspuren finden durch Korrosion der Werkstoffoberflächen, durch Emaillierfehler sowie durch die eingesetzten Chemikalien Eintrag in das Produkt und können durch TXRF- Messungen quantifiziert werden. Über eine Bestimmung der anorganischen Elemente durch TXRF (fingerprint- Analyse) können anhand einer Mustererkennung Arzneistoffchargen unterschieden oder gar entsprechenden Validierungen zugeordnet werden. Die experimentellen Untersuchungen zeigen, daß eine Erfassung von anorganischen Elementspuren in Arzneistoffen durch TXRF nur nach einem Abbau der organischen Matrixanteile in niedermolekulare und leicht flüchtige Verbindungen erfolgen kann. Eine Quantifizierung der anorganischen Spurenbestandteile durch ein direktes Vermessen der Proben ist nicht möglich. Die organischen Matrixanteile führen auf dem Probenträger zu starken Trocknungsrückständen und hohen Comptonstreuquerschnitten. Die durch den Comptoneffekt verursachte Streustrahlung begrenzt die Erfassung von anorganischen Elementen auf Nebenbestandteile. Eine Erfassung von anorganischen Elementen im Nanogramm- Bereich kann nicht erfolgen. Nebengruppenelemente und Elemente mit hohen Ordnungszahlen zeigen dabei gegenüber leichten Elementen aufgrund ihrer größeren Fluoreszenzintensität und energiereichen sekundären Röntgenstrahlung eine höhere Nachweisempfindlichkeit. Aufgrund der hohen Reichweite von harten Röntgenstrahlen in Materie konnte zudem ein Einfluß organischer Matrixanteile auf die Wiederfindungsrate von schweren Elementen nicht beobachtet werden. Leichte Elemente können dagegen aufgrund ihrer weichen sekundären Emissionsstrahlung und die damit verbundenen Absorptionseffekte in organischen Matrices nur unbefriedigend quantifiziert werden. Das Abtrennen der organischen Matrixanteile kann durch einen Naßaufschluß mit Salpetersäure in einem geschlossenen System unter konventioneller und mikrowellenunterstützter Wärmezufuhr sowie durch ein Sauerstoffplasma erfolgen. Die Effizienz eines Naßaufschlusses mit Salpetersäure in einem geschlossenen Gefäß ist dabei abhängig von dem Kohlenstoff- Grundgerüst der Verbindungen. Aliphatische Kohlenwassertsoffe sowie alicyclische und aromatische Heterocyclen werden nahezu vollständig mineralisiert. Aromatische Verbindungen zeigen dagegen einen geringen Kohlenstoff umsatz. Es entstehen aromatische Nitrosoverbindungen, die unter den gegeben Bedingungen nicht weiter abgebaut werden können. Eine Erhöhung des Mineralisierungsgrades konnte auch durch die Bildung von angeregtem Sauerstoff durch Zusatz von geringen Mengen an Wasserstoffperoxid nicht beobachtet werden. Die Ergebnisse zeigen zudem, daß eine Quantifizierung von leicht flüchtigen Elementen in Gegenwart von Stickoxiden aufgrund von Elementverflüchtigungen nicht erfolgen kann. Sauerstoffplasmen führen unabhängig vom Kohlenstoff- Grundgerüst zu einer vollständigen Mineralisierung der organischen Matrixanteile. Infolge des hohen Oxidationspotentials von angeregtem Sauerstoff ist bei dieser Aufschlußtechnik eine quantitative Erfassung von leicht flüchtigen Elementen und Verbindungen nicht möglich.
Entwicklung redoxaktiver para-Hydrochinonliganden und deren Anwendung in der Koordinationschemie
(2006)
Niedrigdimensionale Spinsysteme sind hinsichtlich ihrer magnetischen und elektronischen Eigenschaften von großem Interesse. Einen Zugang zu derartigen Systemen bieten Koordinationspolymere aus paramagnetischen CuII-Ionen (S = ½) und verbrückenden para-Hydrochinon-Liganden. CuII-Ionen eignen sich als Spinträger unter anderem deshalb, weil sie stabile quadratisch-planare Komplexe auszubilden vermögen, wodurch die Entstehung niedrigdimensionaler Strukturen begünstigt wird. Die Attraktivität para-Hydrochinon-basierter Brückenliganden beruht auf deren Redoxaktivität und der Tatsache, dass sie wegen ihrer starren π-konjugierten Struktur in der Lage sind antiferromagnetische Wechselwirkungen zwischen zwei paramagnetischen Metallzentren zu vermitteln. Darüber hinaus sind para-Hydrochinonderivate meist auch in der radikalischen Semichinonform stabil. Hieraus ergibt sich die Möglichkeit in para-Hydrochinon-verbrückte Koordinationspolymere durch elektrochemische Dotierung gezielt zusätzliche ungepaarte Spins zu injizieren. ...
Mit der fortschreitenden Verkleinerung von Prozessoren und Speicherbausteinen in der Mikroelektronik ist der Einsatz neuer Materialien oft unumgänglich. Zur Zeit steht Siliciumdioxid, das als Dielektrikum in Transistoren eingesetzt wird, im Blickfeld des Interesses. Die kleiner werdenden Strukturen führen hier zu dünneren SiO2-Schichten, was bei Schichtdicken unter 2 nm einen Anstieg der Tunnelströme im SiO2 zur Folge hat. Dies stellt für die Bauelemente ein erhöhtes (Kurzschluss-) Risiko dar. Seit geraumer Zeit finden spezielle Speicherzellen große Aufmerksamkeit, in denen Perowskite für die Gate-Oxidschichten zum Einsatz kommen. Sie sind charakterisiert durch hohe Dielektrizitätskonstanten (ε > 20, SiO2 ~ 4 ) oder weisen ferroelektrische Eigenschaften auf. Als interessante Kanditaten für das Dielektrikum gelten zur Zeit BST (Barium-Strontium-Titanat), SBT (Strontium-Bismut-Tantalat) oder PZT (Blei-Zirkonium-Titanat). Die Einführung neuer Materialien in die Chip-Technologie ist immer mit einem Risiko verbunden. Einer der Hauptfaktoren für die Ausbeutelimitierung bei der Produktion von Halbleiterbauelementen ist die Metallkontamination auf Silicium-Oberflächen. Aufgrund ihrer Eigenschaften können Metallverunreinigungen die elektrischen Eigenschaften von Halbleiterbauelementen schädigen. Bisherige Untersuchungen an oben genannten Schichten konzentrierten sich auf das elektrische und physikalische Verhalten. Wenig war bislang bekannt über das Kontaminationsverhalten und dadurch bedingte Auswirkungen/Risiken auf die Bauelemente. Im Rahmen der vorliegenden Arbeit wurden Kontaminationsaspekte, insbesondere während Hochtemperaturprozessen, einiger Metalle auf Silicium (100)-Oberflächen näher untersucht. Das Hauptaugenmerk lag hierbei neben dem Adsorptions- und Desorptionsverhalten auf der Diffusion folgender Elemente: Barium, Strontium, Bismut, Iridium und Platin. Erkenntnisse über die Reaktivität der Metalle bei unterschiedlichen Reaktionsbedingungen sollten mögliche Risikofaktoren des Einsatzes neuer obiger Dielektrikum-Schichten aufzeigen. Die Ergebnisse für die untersuchten Elemente der II. Hauptgruppe, Barium und Strontium sprechen für ein träges Reaktionsverhalten während der Temperprozesse. Unter den vorliegenden Bedingungen wurden die Metalle im nativen oder thermischen Oxid eingelagert (gute Oxidbildner) und ließen sich mittels einer Oxid-Ätzung vollständig von der Si-Oberfläche entfernen. Unabhängig von der Atmosphäre (N2, O2) und der Si-Oberfläche (hydrophil, hydrophob) waren keine Quer-Kontaminationen durch Desorption zu beobachten. Angesichts der starken Tendenz zur Oxid-Bildung bzw. Einlagerung ließ sich keine nennenswerte Diffusion ins Si-Substrat erkennen. Ferner war ein Einfluss auf die Oxidationsrate und Oberflächenrauhigkeit nicht zu beobachten. Mit Blick auf den Einsatz in der CMOS-Technologie stellen Barium und Strontium, wegen ihres geringen Diffusionsvermögens, keine Gefahr für die Si-Substrateigenschaften dar. Sie können jedoch als Verunreinigungen Si-Oxid zu einer Anreicherung an zusätzlichen positiven Ladungen führen und sich negativ auf die Qualität des Oxids auswirken. Bismut präsentierte sich auf hydrophilen Si-Substraten insbesondere unter N2-Atmosphäre als sehr volatil. Dieses Verhalten, höchstwahrscheinlich flüchtiger Bi-Oxide, kann durch Gasphasentransport zu Quer-Kontaminationen benachbarter Si-Substrate führen. Unabhängig von der Temperatmosphäre lassen sich Quer-Kontaminationen ausschließlich auf oxidierten Si-Substraten beobachten, was auf die Notwendigkeit eines bereits vorhandenen dünnen Siliciumoxids als Voraussetzung für eine Quer-Kontamination hindeutet. Eine mögliche Erklärung wäre in der Bildung von weniger flüchtigen Bi-Silikaten zu finden. Die enormen Verluste an Bismut auf hydrophoben Oberflächen finden eine Begründung in dem hohen Abdampfverhalten des vermutlich reduktiv abgeschiedenen Bismuts auf dem Silicium Ähnlich wie Barium und Strontium bevorzugt Bismut den Verbleib im Oxid während Oxidationsprozessen (Bildung von Oxiden und mgl. Bi-Silikaten). Auch hier wiesen die Verunreinigungen keinen Einfluss auf das Oxidwachstum sowie dessen Oberflächenrauhigkeit auf und ließen sich mit einer Oxid-Ätzung von der Si-Oberfläche entfernen. Tiefenprofil- und ELYMAT-Untersuchungen ließen keine Diffusion und schädliche Einflüsse auf die Eigenschaften des Siliciums beobachten. Prozesstechnisch gesehen ist die Bildung möglicher Bi-Silikate unerwünscht, da sie wegen der unterschiedlichen Dichte des SiO2 zu Stress-Regionen auf dem Wafer führen können [21]. Weiterhin besteht gerade in der hohen Flüchtigkeit und Quer-Kontamination ein hohes Kontaminationsrisiko für die Prozess-Apparaturen, andere Wafer und somit der „Verschleppung“ in andere Technologien. Von einer anderen Seite zeigten sich die untersuchten Metalle der Platingruppe, Iridium und Platin. Verunreinigungen an Iridium diffundieren, unabhängig von den RTPBedingungen, ins Si-Substrat und führen zu einer eindeutigen Verringerung der Ladungsträgerlebensdauer („Liftime-Killer“ [45]). Hier zeigten in O2 behandelte Substrate niedrigere Eindringtiefen, was auf eine stärkere Desorption flüchtiger Oxidverbindungen und denkbaren Ir-O-Si-Verbindungen im SiO2 [174] zurückgeht. Parallel hierzu waren Quer-Kontaminationen zu beobachten die durch die Flüchtigkeit von IrO3 erklärt werden können. Ferner führen Verunreinigungen an Iridium zu einem geringeren Oxidwachstum. AFM-Untersuchungen unterstützen die Vermutung einer Ir-Silicidierung an der SiO2/Si-Grenzfläche unter N2-Atmosphäre und forcieren die Bildung von diffusionseinschränkenden Ir-Verbindungen unter O2. Das in der Halbleiter-Technologie bereits eingesetzte Platin ist ausreichend untersucht worden [45] und begleitete die Untersuchungen als Referenzelement. Aus der Literatur bereits bekannt, zeigt Platin ein ausgeprägtes Diffusionsvermögen in das Si-Substrat, unabhängig von dem Temperaturprozess. Dort wirkt es als Generations-/ Rekombinationszentrum und reduziert die Lebensdauer der Ladungsträger. Quer-Kontaminationen waren generell nicht zu beobachten, da unter den vorliegenden Versuchsbedingungen keine flüchtigen Pt-Verbindungen gebildet werden. Dem Iridium ähnlich zeigte Platin bei 1000°C unter O2 im Vergleich eine etwas niedrigere Oxiddicke, was ebenfalls in der Bildung einer Diffusionsbarriere bzw. Pt-O-Si-Bereichen [174] einen möglichen Interpretationsansatz findet. Hinsichtlich des Einsatzes in der Halbleitertechnologie stellen Iridium und Platin wegen ihrer Eigenschaften (hohe Mobilität sowohl im SiO2 und Si, Gasphasentransfer (Ir unter O2), Reduktion der Ladungsträgerlebensdauer) ein enormes Risiko- und Störpotential dar. Während bei Bismut ebenso die Gefahr der Quer-Kontamination besteht, sind die Metalle Barium und Strontium dagegen als weniger kritisch einzustufen.
Methoden zur Präparation und Charakterisierung von time dependent haze auf Siliziumoberflächen
(2002)
Zwischen der Herstellung von Siliziumwafern und ihrer weiteren Verarbeitung zu Halbleiterbauelementen liegt eine Zeitspanne, in welcher die Scheiben in Kunststoffboxen aufbewahrt werden. Während dieser Lagerung kann es zu einem Ansteigen der Oberflächenrauhigkeit kommen. Dieses Phänomen wird als Time Dependent Haze (TDH) bezeichnet und durch chemische Prozesse von Verunreinigungen auf der Siliziumoberfläche verursacht. Diese Kontaminationen entstammen dem Kunststoff der Transportboxen, der Reinraumluft oder den Chemikalien der naßchemischen Waferreinigung. Time Dependent Haze wurde künstlich hergestellt und charakterisiert. Die Präparationen erfolgten in verschiedenen Versuchsreihen mit organischen und anorganischen Verbindungen. Diese gezielten Kontaminationen erlauben Rückschlüsse auf Substanzen und Einflußgrößen, welche TDH verursachen. Nach einer Lagerungsperiode wurden die Siliziumoberflächen mittels Streulichtmessungen untersucht. Das Auftreten von Licht-Punkt-Defekten diente als Maßstab für die TDH-Bildung. Mit verschiedenen analytischen Methoden, insbesondere dem Rasterkraftmikroskop, wurde TDH in einem frühen Entstehungszustand untersucht. Präparationen mit flüchtigen organischen Verbindungen zeigten, daß solche Substanzen TDH erzeugten, die sowohl einen hohen Dampfdruck als auch eine gute Wasserlöslichkeit besitzen. Beide Eigenschaften sind notwendig, um über die Gasphase auf die hydrophile Oberfläche eines Wafers zu gelangen. Die Morphologie dieses TDH fiel sehr unterschiedlich aus. Im Fall der Präparation mit Aceton enstanden Partikel von wenigen Nanometern Durchmesser. Die gezielte Verunreinigung mit Tetrahydrofuran führte zu einem Kontaminationsfilm mit einer sehr geringen Mikrorauhigkeit. Anorganische Verbindungen wie beispielsweise Schwefelsäure, die in der Waferreinigung Verwendung findet, können bei fehlerhaften Reinigungsschritten TDH bilden. Unter dem Einfluß einer solchen Lösung, bestehend aus H2SO4/H2O2, entstanden sulfathaltige Kristallite, welche im Verlauf der Waferlagerung agglomerierten. Das gleiche Resultat ergab eine Präparation, bei der Siliziumwafer einer Atmosphäre aus Schwefeldioxid ausgesetzt waren. Sehr wahrscheinlich existieren die Kristallisationskeime bereits unmittelbar nach der Präparation. Aufgrund ihrer geringen Größe können diese von der Streulichtmessung nicht als Partikel erfaßt werden. Erst nach mehr monatiger Waferlagerung ist das Kristallwachstum soweit fortgeschritten, daß das untere Detektionslimit der Streulichtmethode erreicht wird und die Partikel als solche registriert werden können. Auf Wafern mit organischem TDH konnte Kupfer nachgewiesen werden. Dieses Metall ist als Verunreinigung im Reinstsilizium enthalten. Es diffundiert innerhalb der Lagerungsperiode zur Oberfläche und scheidet sich ab. Dort fungiert Kupfer als Nukleationszentrum für Kontaminanten und fördert auf diese Weise die TDH-Entstehung. Experimente mit mehreren Einflußgrößen, bei welchen Siliziumwafer verschiedenen Parametern gleichzeitig ausgesetzt waren, zeigten synergetische Effekte in Bezug auf die Bildung von Time Dependent Haze. Im Vergleich zu Präparationen mit nur einem Kontaminanten lag die Zahl der neu entstandenen Licht-Punkt-Defekte unerwartet hoch. Innerhalb dieser Versuchsmatrix hatten die Anwesenheit von Ammoniumsulfat und eine hohe Luftfeuchtigkeit einen deutlichen Einfluß auf die TDH-Entstehung. Die Siliziumoberfläche wird durch einzelne Substanzen aktiviert und die Abscheidung weiterer Kontaminationen dadurch erhöht. Eine nähere Untersuchung von TDH bestehend aus verschiedenen Kontaminanten erfolgte mit Hilfe des Pulsed Force Mode/AFM. Diese Methode ermöglicht anhand der Bestimmung der Adhäsion zwischen einer AFM-Meßspitze und der Oberfläche die Unterscheidung verschiedener Materialien mit der hohen Auflösung eines Rasterkraftmikroskops. Zu Beginn der Untersuchungen erfolgte eine Evaluation der Methode. Dabei zeigte sich, daß die Adhäsion unbeeinflußt von der Partikelgröße ist. Das Adhäsionssignal ist abhängig vom Radius der AFM-Spitze und von der umgebenden Luftfeuchtigkeit. Dieses Signal setzt sich zusammen aus der Oberflächenenergie des Materials und aus dem Wasser- und Kontaminationsfilm, welcher die Oberfläche bedeckt. Adhäsionsmessungen an kontaminierten Wafern zeigten außer der rasterkraftmikroskopischen Abbildung der Oberfläche zusätzliche Strukturen. Diese deuten auf das gleichzeitige Auftreten von TDH-Partikeln mit unterschiedlicher Zusammensetzung hin. Die Ergebnisse dieser Arbeit bestätigten ein bereits existierendes Modell zur Entstehung von Time Dependent Haze. Unter Berücksichtigung der neuen Erkenntnisse konnte dieses Modell erweitert werden.
Die vorliegende Arbeit fasst folgende experimentellen Arbeiten zusammen: • Synthese von amorphem, schwarzem, basischem Silicium Si am,schw,ox und amorphem, schwarzem, nicht basischem Silicium Siam,schw durch Reduktionsreaktion von Siliciumtetrachlorid mit Natrium. • Reaktivität des amorphen Siliciums Si am gegenüber verschiedenen Gasen: Cl2, HCl, CH3Cl • Reaktivität von Si am gegenüber Alkoholen bei Raumtemperatur. • Reaktivität von Si am gegenüber Alkoholen und Essigsäure in einem geschlossenen System, nicht katalysiert/katalysiert durch Cu(I)Cl und Cu(I)O. • Reaktivität von Si am,schw,ox und Si am,schw gegenüber Alkoholen und Essigsäure in einem offenen System (Ofen, „slurry phase“-Reaktor), nicht katalysiert/katalysiert durch Cu(I)Cl und Cu(I)O. • Thermische und katalytische Disproportionierungsreaktionen von Methylmethoxysilanen, katalysiert durch Alkalimetalle (Na), salzartige Verbindungen (Ca(OH)2, MgSO4/C, Na2SO4/C und (NH4)2SO4/C) und Lewis-Säuren (AlCl3). • Komproportionierung zwischen Trimethylmethoxysilan und Methyltrimethoxysilan Der Schwerpunkt dieser Arbeit lag in Untersuchung der chemischen Reaktivität von amorphem Silicium Si am, synthetisiert durch Na-Reduktion von Siliciumtetrachlorid, gegenüber verschiedenen Gasen, wie z. B. Chlorgas, Chlorwasserstoff und Methylchlorid, gegenüber Alkoholen, wie z. B. Methanol, Ethanol und Phenol und gegenüber Essigsaure unter unterschiedlichen Reaktionsbedingungen. Die Reaktion zwischen amorphem Silicium Si am und Cl2-Gas führt bei 240-250°C zu Tetrachlorsilan SiCl4 als einziges Produkt. Die Reaktion mit HCl-Gas liefert im Temperaturbereich zwischen 360-370°C zwei Produkte: 15% Dichlorsilan, H2SiCl2 und 85% Trichlorsilan, HSiCl3. Im Temperaturbereich zwischen 370-420°C entstehen drei Produkte: 36,4% Dichlorsilan H2SiCl2, 58,5% Trichlorsilan HSiCl3 und 5,1% Tetrachlorsilan SiCl4. Über eine Temperaturführung kann die Produktbildung wesentlich beeinflusst und damit auch gesteuert werden. Durch eine Reaktion mit Methylchlorid bei 560°C entstehen zwei Produkte: 79% Methyltrichlorsilan CH3SiCl3 und 21% Dimetyldichlorsilan (CH3)2SiCl2. Basisches Silicium Siam,schw,ox liefert in den Reaktionen mit Alkoholen und Essigsäure unter Rückfluss-Bedingungen (Temperaturen zwischen 20 und 420°C; offene Reaktionssysteme) jeweils ein einziges Produkt und führt mit den korrespondierenden Partnern selektiv zu Tetramethoxy-, Tetraethoxy-, Tetraphenoxy- und Tetraacetoxysilan. Diese Reaktionen werden durch die im eingesetzten Siam/NaCl-Gemisch vorhandene Base (NaOH, Na2Ox; x = 1, 2) katalysiert. Gemischte Alkylalkoxysilane oder Siloxane entstehen unter den vorgegebenen Bedingungen nicht. Silicium setzt sich dabei in den Reaktionen mit Methanol und Ethanol vollständig um. Werden die Bedingungen modifiziert und die Reaktionen in geschlossenen Systemen (Reaktionsampullen) bei 150°C, katalysiert durch 5 Gew. % Cu(I)Cl im Mol-Verhältnis Si am,schw,ox/CH3OH 1:3 und 1:4 durchgeführt, wird Trimethoxysilan in 91% und 84% Ausbeute gewonnen. Der Produktbildungsweg führt offensichtlich über die Katalyse eines Komplexes Na+[Cu(OH)Cl]-, der in situ aus Cu(I)Cl und NaOH gebildet wird. Nicht basisches Silicium, Siam,schw, reagiert mit Methanol bei Raumtemperatur zu Trimethoxysilan HSi(OCH3)3 (16-18%) und zu Tetramethoxysilan Si(OCH3)4 (84-82%). Die Produktbildung kann durch Änderungen Reaktionsbedingungen in Richtung von Trimethoxysilan verschoben werden. So entsteht Trimethoxysilan in einer geschlossenen Ampulle zu 95% als Hauptprodukt der Reaktion zwischen amorphem Silicium und Methanol im Mol-Verhältnis 1:3 in Anwesenheit von NH4HF2 als Aktivator. 84,5% Trimethoxysilan entstehen in einer Ampulle bei 200°C nach 5 Stunden Reaktionszeit, dann wenn Methanol im stöchiometrischen Verhältnis 8:1 eingesetzt wird. Der Umsatz an Silicium ist praktisch vollständig (100%). Wird die Reaktion zwischen Siam,schw und Methanol in einem „slurry phase“-Reaktor durchgeführt, resultiert eine Abhängigkeit der Produktausbeute vor allem vom Lösungsmittel, dann aber auch von den weiteren Bedingungen. In Dodecylbenzol entsteht das Trimethoxysilan bei 230°C und mit Cu(I)O als Katalysator zu 72% in einer 8-stündigen Reaktion. Unter vergleichbaren Bedingungen, aber in Isoparaffinöl bildet sich Trimethoxysilan zu 61%. In einem modifizierten „slurry phase“-Reaktor, in dem die Produkte mit überschüssigem Methanol sofort aus der Reaktion abgeführt werden, entsteht das Trimethoxysilan nicht. Allerdings bilden sich in diesem Fall methylierte Methoxysilane. Der Umsatz an Silicium hängt auch von der Temperatur des Methanol-Dampfes ab. Wird die Temperatur zwischen 150-200°C gehalten, werden 49% des Siliciums umgesetzt. Ansonsten beträgt die Umsatzrate des Siliciums 20-25%. Amorphes, schwarzes, basenfreies Silicium, Si am,schw, reagiert bei 150°C mit Ethanol im Mol-Verhältnis 1:3 zu 91% und bei 200°C (Mol-Verhältnis Si : EtOH 1:8) zu 86% Triethoxysilan, HSi(OEt)3. Die Reaktion zwischen nicht basischem Silicium Si am,schw und Essigsäure liefert in der Siedehitze kein Tetraacethoxasilan, sondern nur Polyacethoxysilane mit einem Polymerisationsgrad von n = 2, 3, in einer Ampulle bildet sich jedoch ein Gemisch aus Tetraacetoxysilan und verschiedenen Acethoxypolysilanen. Die Polysilanbildung verstärkt sich mit zunehmender Reaktionstemperatur und –dauer. Die Reaktion zwischen Si am,schw und Essigsäure in einem offenen System (Ofen) liefert bei 300°C außer Tetraacetoxysilan ein Gemisch von Acethoxypolysilanen mit n=2-6. Versuche zur Bildung von Phenoxsilanen aus Si am,schw. und Phenol schlugen bei Temperaturen zwischen 150-300°C fehl. Das MALDI-TOF-MS-Spektrum einer bei 225-230°C im Vakuum siedenden Fraktion, die aus Reaktion von Si am,schw mit Phenol bei 420°C im Ofen entstanden ist, zeigt Spuren von Tetraphenoxysilan und organische Polymere mit dem Molekulargewichht bis zu 960 Dalton. Während Umsetzungen von amorphem Silicium mit Methanol in geschlossenen Reaktionsampullen Trimethoxysilan und Tetramethoxysilan als Hauptprodukte liefern, bilden sich in einem offenen System methylierte Methoxysilane MenSi(OMe)4-n (n=1, 2) in unterschiedlichen Ausbeuten. Dimethyldimethoxysilan entsteht aus basischem Silicium Siam,schw,ox nicht; selbst durch Katalysatorzusatz entsteht das gewünschte Produkt nur in Spuren. Die Monomethylierung verläuft dagegen erfolgreicher. Die höchste Ausbeute an Methyltrimethoxysilan (33,7%) wird bei 320°C mit 20 Gew. % Cu(I)Cl als Katalysator erzielt. Völlig anders verhält sich nicht basisches Silicium Si am,schw , denn es reagiert mit Methanol in einem offenen System bei 350°C zu 13% Dimethyldimethoxysilan (CH3)2Si(OCH3)2, und 37% Methyltrimethoxysilan CH3Si(OCH3)3. In Reaktionen mit größeren Silicium-Mengen (Si-Gehalt: 39-60 mmol) entstehen in einem nicht gerührten Reaktionsreaktor nach 20’ Minuten Reaktionszeit bei 300°C 26% Dimethyldimethoxysilan (CH3)2Si(OCH3)2 und nach 45’ Minuten Reaktionszeit 49,5% Methyltrimethoxysilan CH3Si(OCH3)3. In einem nicht gerührten Reaktionsrohr entstehen nach 3 Stunden Reaktionszeit 25-30% Dimethyldimethoxysilan bei 300°C und mit 20 Gew. % Kupfer(I)Chlorid als Katalysator. In einem gerührten Reaktionsrohr bilden sich bei 350°C und mit 20 Gew. % Cu(I)Cl nach 3-stündiger Reaktion 23,5% (CH3)2Si(OCH3)2 und 53,3% CH3Si(OCH3)3. Das Vorhandensein des Katalysators erhöht die Ausbeute an methylierten Methoxysilanen in den Reaktionen zwischen nicht basischem Silicium und Methanol. Aus dem Verlauf der Reaktion im Ofen lässt sich schließen, dass die größte Menge des Dimethyldimethoxysilans, (CH3)2Si(OCH3)2, während der ersten 20-40 Minuten entsteht. Danach sinkt der Anteil mit zunehmender Reaktionszeit, es bilden sich verstärkt die festen Dimethyloligosiloxane. Die Ausbeute an Tetramethoxysilan, Si(OCH3)4, wächst mit der Reaktionszeit kontinuierlich. Dagegen bleibt die Ausbeute an Methyltrimethoxysilan, CH3Si(OCH3)3, während 3-stündiger Reaktion relativ konstant. Die Bildung aller drei Produkte wurde zwischen 300° und 350°C detailliert verfolgt. Nur ca. 20% des Siliciums setzen sich zu den flüchtigen Produkten um, rund 80% Silicium bleiben in fester Form als nicht abreagiertes Silicium und als feste Oligodimethylsiloxane erhalten. Eine nicht katalysierte Reaktion zwischen Si am,schw und Ethanol liefert nach 3h Reaktionszeit in einem nicht rührenden Reaktor etwa 23% HSi(OCH3)3 und etwa 72% Si(OEt)4. Etylenethoxysilane oder -siloxsane bilden sich nicht. Zum Weiteren ist es gelungen, Dimethyldimethoxysilan durch Disproportionierungsreaktion aus Methyltrimethoxysilan und Tetramethoxysilan über metallischem Natrium im Mol-Verhältnis 1:1 in einer Ampulle bei 250°C herzustellen. Aus Disproportionierung von Methyltrimethoxysilan sind 12% Dimethyldimethoxysilan zu erhalten. Die Disproportionierung von Tetramethoxysilan führt zu 27% Dimethyldimethoxysilan, (CH3)2Si(OCH3)2, 34% Methyltrimethoxysilan, CH3Si(OCH3)3, und 11% Trimethylmethoxysilan, (CH3)3SiOCH3. Die Menge des eingesetzten Natriums muss in weiteren Arbeiten noch optimiert werden. Eine Komproportionierungsreaktion zwischen Trimethylmethoxysilan, (CH3)3SiOCH3, und Methyltrimethoxysilan, CH3Si(OCH3)3, zu Dimethyldimethoxysilan, (CH3)2Si(OCH3)2, fand unter den in dieser Arbeit beschriebenen Bedingungen nicht statt. Diese Ergebnisse sind ein im Labormaßstab chlorfreies Verfahren zur Herstellung von methylierten Methoxysilanen. Unter der Voranstellung der Aufskalierbarkeit wird damit eine neue Route eines möglicherweise technisches Prozesses (das Q-Verfahren) zu Darstellung von Siliconen zugänglich; diese führt wie folgt aus: Siliciumtetrachlorid → amorphes Silicium → Tetramethoxysilan/Tetraethoxysilan/Tetraacetoxysilan → Methylmethoxysilane → Silicone. Es gilt nun, die Synthesebedingungen nach erfolgreicher Optimierung in den Pilotmaßstab zu überführen. Die Synthese von Trimethoxysilan, HSi(OCH3)3, erscheint bereits jetzt schon den Bedingungen des technisch durchführenden Cromptonprozesses überlegt zu sein. Diese bietet jedoch den Vorteil, von technisch verfügbarem Silicium anzugehen. Eine exakte und vergleichende Prozess-Analyse wird darüber Aufschluss geben, ob die in dieser Arbeit erworbenen Ergebnisse zu einer technischen Umsetzung führen.
In der vorliegenden Arbeit ist es gelungen, OTS-, MPTMS-, und MPTMS/OTS gemischte SAMs aus der Lösung auf SC-1 chemisch oxidierten Siliziumwafern („SiO2“) zu präparieren. Die Adsorption der OTS oder MPTMS SAMs auf SiO2 wird von zwei konkurrierenden Reaktionen bestimmt, d.h. „Selbstaggregation” in der Ausgangslösung und “Oberflächendehydration” des SiO2 -Substrates. Die beiden Alkylsiloxan-SAMs weisen unterschiedliches Bildungsverhalten auf. Die Reifungsdauer der Ausgangslösung vor der Adsorption wirkt sich signifikant auf die Bildung der OTS SAMs aus, demgegenüber ist bei MPTMS SAMs kein Einfluß zu beobachten. Für OTS SAMs sind große Dendriten oftmals von kleinen Rundinseln umgeben, dagegen für MPTMS SAMs treten prinzipiell nur sporadisch verteilte kleine Rundinseln auf. Die Abwesenheit des Chlor-Signals in XPS-Spektren bestätigt, dass innerhalb der Adsorption die Si-Cl Bindungen der OTS-Moleküle zum größten Teil hydrolysiert werden. Doch für MPTMS SAMs ist in C 1s-Spektren ein Peak bei 286.4 eV, der der unhydrolysierten Si-OCH3 Bindung entspricht, zu beobachten. Die Hydrolysefähigkeit der Si-Cl Bindung des OTS ist erwartungsgemäß stärker als jene der Si-OCH3 Bindung des MPTMS. Diese Tendenz samt dem Unterschied in der Alkylkettenlänge wirkt sich beträchtlich auf die Bildung und die Morphologie der adsorbierten Inseln aus. Bei gleicher Konzentration (5 mM) und Reifungsdauer der Ausgangslösung bilden sich OTS SAMs viel schneller als MPTMS SAMs bei Raumtemperatur. Sie hat auch eine größere Oberflächenbedeckung wegen der seitlichen Vernetzung zur Folge. Diese Beobachtung zeigt eine prognostizierbare kinetische Schwierigkeit zur Präparation der OTS/MPTMS gemischten SAMs durch Koadsorption. Grund hierfür ist, dass die Adsorption voraussichtlich von OTS-Molekülen dominiert wird. Darüber hinaus ist Aggregation zwischen hydrolysierten OTS- und MPTMS-Molekülen nicht ausgeschlossen. Neben der Koadsorption steht in der zweistufigen Adsorption ein weiteres herkömmliches Verfahren zur Verfügung. Das Endprodukt kann nach der Reaktionsreihe der Silane mit „OTS+MPTMS“ oder „MPTMS+OTS“ gemischte SAMs bezeichnet werden. Unter Berücksichtigung der individuellen Oberflächenbedeckung und Morphologie wurde eine Rezeptur aufgestellt, in der die Adsorption jeweils höchstens 30s (für OTS) und 20 min (für MPTMS) dauert. Angesichts der vielfältigen Inselstruktur, d.h. Monoschicht, polymerisierte Bälle, und sogar Multischicht, ist eine Phasenunterscheidung nach der Dicke, z.B. mittels AFM, nicht zu erwarten. Die Existenz der lateralen unvernetzten Si-OH Gruppen der adsorbierten OTS-Inseln könnte die Präparation der homogenen OTS+MPTMS gemischten SAMs erschweren. In diesem Fall ist es fraglich, ob die hydrolysierten MPTMS-Moleküle vollständig wie geplant mit oberflächnahen OH-Gruppen von SiO2 reagieren. Mit einer umgekehrten Reaktionsreihe löst sich das Problem von selbst, da die adsorbierten MPTMS-Inseln hauptsächlich unhydrolysierte seitliche Si-OCH3 Gruppen besitzen. Die morphologische Erkennbarkeit unterstützt die Machbarkeit der Präparation der MPTMS+OTS gemischten SAMs. Die unterschiedlichen Messmodi des AFM, mit denen die Morphologie der OTS SAMs aufgenommen wurde, ergaben deutliche Unterschiede in ihrem Erscheinungsbild. Im Vergleich zum Tappingmodus sind die Grenzen der OTS-Inseln auf Kontaktmodus-Bildern nur undeutlich erkennbar. Die großen Inseln erscheinen nicht so dendritisch. Die Ursache dieser Phänomene könnte am Wassermeniskus zwischen Spitze und Probe liegen, da die Messung nicht in Flüssigkeit, sondern an Luft durchgeführt wurde. Auf LFM-Bildern sind die adsorbierten OTS-Inseln heller als unbedecktes SiO2, während die MPTMS-Inseln dunkler als SiO2 aussehen. Eine ähnliche Auswirkung der Messmodi auf die Morphologie der MPTMS SAMs wurde nicht beobachtet. Durch die Adsorption von 1-Decanthiol lässt sich die Si3N4-AFM-Spitze modifizieren. Eine solche CH3-terminierte Spitze ist hydrophob und verursacht einen gegenteiligen Helligkeitskontrast auf LFM-Bildern der adsorbierten OTS-Inseln.
In der Arbeit wurden neue Komplexbildner für die nasschemische, alkalische Reinigung von Siliciumhalbleiteroberflächen vorgestellt. Dabei handelte es sich neben kommerziell verfügbaren Verbindungen, wie beispielsweise Tiron, um den Chelatbildner Pyrinan und die vielversprechende Gruppe der 3-Hydroxypyridin-4(1H)-on-Komplexbildner („Pyridinone“). Insbesondere Letztere sind als effiziente Eisenkomplexbildner von präklinischen Untersuchungen zur Therapie von Eisenstoffwechselerkrankungen bekannt und haben deshalb großes Interesse hervorgerufen. Die Darstellung von Pyrinan und der Pyridinone war in befriedigenden bis guten Ausbeuten mit herkömmlichen Syntheseschritten möglich. Die Synthese konnte somit die im Abschnitt 1.2.1 erwähnten Anforderungen an die Komplexbildner befriedigen. Hinsichtlich der an die Strukturierung von Halbleitermaterialen geknüpften, jedoch bei der Präparation der Komplexbildner nicht realisierten Reinheitsbedingungen, wiesen diese einen teilweise erheblichen Kontaminationsgrad durch Metalle auf. Demzufolge hätten die Komplexbildner als potentielle Kontaminationsquellen bei der SC1-Reinigung von Siliciumsubstraten wirken können. Letzteres konnte jedoch im Rahmen der zehnminütigen Immersionsdauer in ¼/20 SC1 bei 70 °C weitgehend ausgeschlossen werden. Der Trend bei der nasschemischen Reinigung von Halbleitersubstraten mit immer stärker verdünnten Reinigunslösungen und reduzierten Reinigungsbadtemperaturen zu arbeiten, sollten dieses und die folgend zusammengefassten Ergebnisse noch weiter begünstigen. Es wurden Reinigungsexperimente mit Siliciumsubstraten und mit den Reinigungslösungen absichtlich zugesetzten Kontaminanten durchgeführt, um die Wirkungen der einzelnen Verbindungen besser studieren zu können. Es wurden die Metalle Al, Fe, Zn, Cu, Ni und Cr, die in der Halbleiterproduktion als gängige Kontaminanten auftreten, untersucht. Die Metalle Zn, Ni und Cu spielen in der SC1-Lösung, mit abnehmender Gewichtung in der genannten Reihenfolge, aufgrund deren Amminkomplexbildung keine nennenswerten Rolle als Oberflächenkontaminanten. Cr(III) wird in der SC1-Lösung zu Chromat oxidiert und kontaminiert aus diesem Grund die Oberfläche ebenfalls nicht. Dem gegenüber sind Al und Fe unter den gewählten Bedingungen sehr starke Oberflächenkontaminanten. Prinzipiell eignen sich fast alle untersuchten Komplexbildner, die Siliciumoberfläche vor der Kontamination durch Fe aus SC1 zu schützen. Hinsichtlich ihrer Wirksamkeit gegenüber Al und Zn wurden sie jedoch deutlich diskriminiert. Daraus schlussfolgernd ist der Einsatz mehrerer Komplexbildnern erforderlich, um die Kontaminationsgefahr der Siliciumoberfläche durch alle genannten Metalle gezielt kontrollieren und über einen gewissen Schwellenwert vermeiden zu können. Die Wirkung von Pyrinan und der Pyridinone ist vergleichbar, meistens jedoch deutlich besser, als die herkömmlicher Poly(alpha-aminomethylencarbonsäuren) (z. B. EDTA, Untersuchungen von IMEC). Sie erzielen Oberflächenkonzentrationen kritischer Kontaminanten (z. B. Fe) in der Größenordnung, die für die Prozessierung aktueller und künftiger Generationen von Bauelementen erforderlich sind. Konsequenterweise sind deshalb sowohl Pyrinan als auch die Pyridinonkomplexbildner und deren Verwendungszweck zum Patent angemeldet worden. In einem weiteren Teil der Arbeit wurde die Eignung der Komplexbildner bestimmt, hochkonzentrierte, den Halbleiterspezifikationen entsprechende Lösungen von H2O2 stabilisieren zu können. Die Stabilität wurde in Abhängigkeit von drei vorgegebenen Lagerungstemperaturen verfolgt. Sowohl die vorgestellten Verbindungen als auch die als Referenzsubstanz mituntersuchte Verbindung Dequest® 2060s konnten die an einen geeigneten Stabilisator gestellten Bedingungen nicht befriedigen. Lediglich die nicht stabilisierte Lösung von H2O2, die Referenzprobe, besaß eine, über den gesamten Beobachtungszeitraum ausreichende Stabilität. Das mangelhafte Abschneiden der vorgestellten Verbindungen als potentielle Stabilisatoren wird deren partieller bzw. vollständiger Oxidation durch H2O2 zugeordnet und ist am Beispiel von Dequest® 2060s weiter diskutiert worden. Im Zuge der Oxidation werden die intrinsischen Metallkontaminationen der Komplexbildner freigesetzt, wodurch die Kontaminanten in die Lage versetzt werden können, in das Reaktionsgeschehen katalytisch einzugreifen und die Zersetzung der Proben zu beschleunigen. Die Lagerung der Komplexbildner in konzentriertem NH3 stellt die Alternative zur Lagerung in H2O2 dar, wenn man zu einem fertig einsetzbaren, industriellen Produkt für die nasschemische Reinigung von Halbleiteroberflächen gelangen möchte, welches eine einstufige alkalische Reinigung (APM+®) ermöglicht. Hier konnten bis auf die Proben, welche Tiron als Komplexbildner enthielten, keine Besonderheiten festgestellt werden. Die mit Tiron versetzten Proben führen bereits nach sehr kurzer Lagerungsdauer zu einer intensiv rot gefärbten Lösung, die der im Alkalischen und durch Luftsauerstoff erfolgenden Oxidation von Tiron durch Luftsauerstoff zugerechnet wird. Eine, die Reinigungsexperimente ergänzende und wichtige Information, stellt die Stabilität der Komplexbildner und durch diese bedingt die der gesamten Reinigungslösung dar. Letztere wurde durch die titrimetrische Bestimmung der Konzentration von H2O2 ausgesuchter Reinigungslösungen bestimmt. Die Stabilität des Komplexbildners DEHP wurde stellvertretend für die ganze Gruppe (der einfachen Pyridinone) in verschiedenen, in der Halbleiterfertigung üblichen, alkalischen, H2O2 enthaltenden Reinigungslösungen untersucht. Die Stabilitätsbestimmungen von DEHP, ausgedrückt in Form dessen Halbwertszeit der Zersetzung in den Reinigungslösungen, wurden mit Hilfe der UV/Vis-Spektralphotometrie durchgeführt. Im Zuge der Stabilitätsbestimmungen wurde festgestellt, dass der Komplexbildner DEHP die Reinigungslösungen zwischen drei (im Fall von 1,65/1/5 TPM) bis vier (im Fall von ¼/20 SC1 und von 1,65/1/5 NC) Halbwertszeiten zu stabilisieren vermag. Darüber hinaus wurde festgestellt, dass DEHP die niedrigste Halbwertszeit in Reinigungslösungen mit TMAH als Base und die höchste in solchen mit Cholin besitzt. Die in den ¼/20-SC1-Lösungen, also mit NH3 als Base, nimmt die mittlere Stellung der drei untersuchten Typen von Reinigungslösungen ein. Diese Abstufung der Stabilitäten wird einerseits dem individuellen komplexierenden Potential der einzelnen Basen als auch der von Cholin vermuteten Rolle, in der Reinigungslösung als Opferreduktionsmittel zu wirken und damit die Lebensdauer (Halbwertszeit) des Komplexbildners zu fördern, zugeordnet. Die UV/Vis-Spektralphotometrie hat sich darüber hinaus bei den Untersuchungen als einfach handhabbares und möglicherweise auch leicht automatisierbares Quantifizierungsverfahren zur Implementierung in bereits bestehende Reinigungsanlagen erwiesen.