We fabricated memristive devices using focused electron beam-induced deposition (FEBID) as a direct-writing technique employing a Pt/TiO2/Pt sandwich layer device configuration. Pinching in the measured current-voltage characteristics (i-v), the characteristic fingerprint of memristive behavior was clearly observed. The temperature dependence was measured for both high and low resistive states in the range from 290 K down to about 2 K, showing a stretched exponential behavior characteristic of Mott-type variable-range hopping. From this observation, a valence change mechanism of the charge transport inside the TiO2 layer can be deduced.
Computational workflow optimization for magnetic fluctuation measurements of 3D nano-tetrapods
(2021)
The detailed understanding of micro–and nanoscale structures, in particular their magnetization dynamics, dominates contemporary solid–state physics studies. Most investigations already identified an abundance of phenomena in one–and two–dimensional nanostructures. The following thesis focuses on the magnetic fingerprint of three–dimensional CoFe nano–magnets, specifically the temporal development of their hysteresis loop. These nano–magnets were grown in a tetrahedral pattern on top of a highly susceptible home–build GaAs/AlGaAs micro–Hall sensor using focused electron beam induced deposition (FEBID).
During the measurements, utmost efforts were employed to exemplify current best research practices. The data life cycle of the present thesis is based upon open–source data science tools and packages. Data acquisition and analysis required self–written automated algorithms to handle the extensive quantity of data. Existing instrumental-controlling software was improved, and new Python packages were devised to analyze and visualize the gathered data. The open–source Python data analysis framework (ana) was developed to facilitate computational reproducibility. This framework transparently analyses and visualizes the gathered data automatically using Continuous Analysis tools based on GitLab and Continuous Integration. This automatization uses bespoke scripts combined with virtualization tools like Docker to facilitate reproducible and device–independent results.
The hysteresis loops reveal distinct differences in subsequently measured loops with identical initial experimental parameters, originating from the nano–magnet’s magnetic noise. This noise amplifies in regions where switching processes occur. In such noise–prone regions, the time–dependent scrutinization reveals presumably thermally induced metastable magnetization states. The frequency–dependent power spectral density uncovers a characteristic 1/f² behavior at noise–prone regions with metastable magnetization states.
Focused electron-beam-induced deposition (FEBID) is a highly versatile direct-write approach with particular strengths in the 3D nanofabrication of functional materials. Despite its apparent similarity to other 3D printing approaches, non-local effects related to precursor depletion, electron scattering and sample heating during the 3D growth process complicate the shape-true transfer from a target 3D model to the actual deposit. Here, we describe an efficient and fast numerical approach to simulate the growth process, which allows for a systematic study of the influence of the most important growth parameters on the resulting shape of the 3D structures. The precursor parameter set derived in this work for the precursor Me3PtCpMe enables a detailed replication of the experimentally fabricated nanostructure, taking beam-induced heating into account. The modular character of the simulation approach allows for additional future performance increases using parallelization or drawing on the use of graphics cards. Ultimately, beam-control pattern generation for 3D FEBID will profit from being routinely combined with this fast simulation approach for optimized shape transfer.
We present experimental results and theoretical simulations of the adsorption behavior of the metal–organic precursor Co2(CO)8 on SiO2 surfaces after application of two different pretreatment steps, namely by air plasma cleaning or a focused electron beam pre-irradiation. We observe a spontaneous dissociation of the precursor molecules as well as autodeposition of cobalt on the pretreated SiO2 surfaces. We also find that the differences in metal content and relative stability of these deposits depend on the pretreatment conditions of the substrate. Transport measurements of these deposits are also presented. We are led to assume that the degree of passivation of the SiO2 surface by hydroxyl groups is an important controlling factor in the dissociation process. Our calculations of various slab settings, using dispersion-corrected density functional theory, support this assumption. We observe physisorption of the precursor molecule on a fully hydroxylated SiO2 surface (untreated surface) and chemisorption on a partially hydroxylated SiO2 surface (pretreated surface) with a spontaneous dissociation of the precursor molecule. In view of these calculations, we discuss the origin of this dissociation and the subsequent autocatalysis.
Vanadium and Manganese Carbonyls as Precursors in Electron-Induced and Thermal Deposition Processes
(2022)
The material composition and electrical properties of nanostructures obtained from focused electron beam-induced deposition (FEBID) using manganese and vanadium carbonyl precursors have been investigated. The composition of the FEBID deposits has been compared with thin films derived by the thermal decomposition of the same precursors in chemical vapor deposition (CVD). FEBID of V(CO)6 gives access to a material with a V/C ratio of 0.63–0.86, while in CVD a lower carbon content with V/C ratios of 1.1–1.3 is obtained. Microstructural characterization reveals for V-based materials derived from both deposition techniques crystallites of a cubic phase that can be associated with VC1−xOx. In addition, the electrical transport measurements of direct-write VC1−xOx show moderate resistivity values of 0.8–1.2 × 103 µΩ·cm, a negligible influence of contact resistances and signatures of a granular metal in the temperature-dependent conductivity. Mn-based deposits obtained from Mn2(CO)10 contain ~40 at% Mn for FEBID and a slightly higher metal percentage for CVD. Exclusively insulating material has been observed in FEBID deposits as deduced from electrical conductivity measurements. In addition, strong tendencies for postgrowth oxidation have to be considered.
Die vorliegende Dissertation behandelt das Thema der Wechselstromleitfähigkeit nano-granularer Metalle, welche mit Hilfe der fokussierten elektronenstrahlinduzierten Direktabscheidung (FEBID) hergestellt wurden, sowie der dielektrischen Relaxation in metall-organischen Gerüstverbindungen (MOFs). Sie war eingebettet in das interdisziplinäre Projekt „Dielectric and Ferroelectric Surface-Mounted Metal-Organic Frameworks (SURMOFs) as Sensor Devices“ im Rahmen des DPG-Schwerpunktsprogramms „Coordination Networks: Building Blocks for Functional Systems“ (SPP 1928, COORNETs). Dabei verfolgt sie ein Sensorkonzept zur selektiven Detektion von Analytgasen. Der zentrale Erfolg der Arbeit besteht dabei in neuen Erkenntnissen über die Wechselstromleitfähigkeit nano-granularer Pt(C)-FEBID-Deponate. Die hierbei gewonnen Erkenntnisse können in Zukunft einen weiteren Baustein in der theoretischen Beschreibung dieses grundlegend interessanten und für sensorische Anwendungen wichtigen Teilgebiets der Festkörperphysik darstellen.